Nozzles, and components thereof and methods for making the same

ABSTRACT

Various nozzles, components of nozzles, and methods, materials and devices for making them are disclosed.

CROSS-REFERENCE TO RELATED APPLICATIONS

Priority is claimed to U.S. Provisional Patent Application Ser. No. 60/303,373 filed on Jul. 6, 2001.

BACKGROUND

In the past, various nozzle structures and materials were known. Wear and durability were considerations with respect to those nozzle structures and materials.

SUMMARY

Various nozzles, components of nozzles, and methods, materials and devices for making them are disclosed.

BRIEF DESCRIPTION OF DRAWINGS

FIGS. 1A-1BB depict sintering of a polycrystalline diamond compact.

FIGS. 1C & 1D depict formation of a diamond table on a substrate by a CVD, PVD or laser deposition method.

FIGS. 3-12 depict preparation of superhard materials for use in making a nozzle component.

FIGS. 13-36 depict final preparation of superhard materials prior to sintering.

FIG. 37 depicts the anvils of a cubic press that may be used in making superhard nozzle components.

FIGS. 38-50 depict machining and finishing superhard nozzle components.

FIGS. 51 a-114 b depict various configurations of nozzles with superhard surfaces.

DETAILED DESCRIPTION

Various embodiments of the devices disclosed herein relate to superhard surfaces for nozzles and components of various compositions and shapes, methods for making those superhard surfaces for nozzles and components, and products, which include those superhard surfaces for nozzles and components. More specifically, some embodiments of the devices relate to diamond and sintered polycrystalline diamond surfaces and nozzles that include diamond and polycrystalline diamond surfaces. Some embodiments of the devices utilize a polycrystalline diamond compact (“PDC”) to provide a very strong, low friction, long-wearing surface in a nozzle. Any surface, including surfaces outside the field of nozzles, which experience wear and require strength and durability will benefit from advances made here.

The table below provides a comparison of sintered polycrystalline diamond (“PCD”) to some other materials. TABLE 1 COMPARISON OF SINTERED PCD TO OTHER MATERIALS Thermal Specific Hardness Conductivity CTE Material Gravity (Knoop) (W/m K) (×10⁻⁶) Sintered 3.5-4.0 9000 900 1.50-4.8  Polycrystalline Diamond Compact Cubic Boron 3.48 4500 800 1.0-4.0 Nitride Silicon Carbide 3.00 2500 84 4.7-5.3 Aluminum Oxide 3.50 2000 7.8-8.8 Tungsten Carbide 14.6 2200 112 4-6 (10% Co) Cobalt Chrome 8.2 43 RC 16.9 Ti6Al4V 4.43 6.6-17.5 11 Silicon Nitride 3.2 14.2 15-7  1.8-3.7

In view of the superior hardness of sintered PCD, it is expected that sintered PCD will provide improved wear and durability characteristics.

Reference will now be made to the drawings in which the various elements of the present devices will be discussed. Persons skilled in the design of nozzles and other surfaces will understand the application of the various embodiments of the devices and their principles to nozzles of all types, and components of nozzles, and devices other than those exemplified herein.

As discussed in greater detail below, the nozzle or nozzle component may use a polycrystalline diamond compacts in order to form durable surfaces. In a polycrystalline diamond compact that includes a substrate, the diamond table may be chemically bonded and mechanically fixed to the substrate in a manufacturing process that may use a combination of high pressure and high temperature to form the sintered polycrystalline diamond. Alternatively, free-standing sintered polycrystalline diamond absent a substrate may be formed. The chemical bonds between diamond and a solvent-catalyst metal are established during the sintering process y combinations of unsatisfied sp3 carbon bonds with unsatisfied substrate metal bonds. Where a substrate is used, the mechanical bond strength of the diamond table to the substrate that results is a consequence of shape of the substrate and diamond table and differences in the physical properties of the substrate and the diamond table as well as the gradient interface between the substrate and the diamond table. The resulting sintered polycrystalline diamond compact forms a durable nozzle or component.

The diamond table may be polished to a very smooth and glass-like finish to achieve a very low coefficient of friction.

While there is discussion herein concerning polycrystalline diamond compacts, the following materials could be considered for forming a nozzle or nozzle component: polycrystalline diamond, monocrystal diamond, natural diamond, diamond created by physical vapor deposition, diamond created by chemical vapor deposition, diamond like carbon, carbonado, cubic boron nitride, hexagonal boron nitride, or a combination of these, cobalt, chromium, titanium, vanadium, stainless steel, niobium, aluminum, nickel, hafnium, silicon, tungsten, molybdenum, aluminum, zirconium, nitinol, cobalt chrome, cobalt chrome molybdenum, cobalt chrome tungsten, tungsten carbide, titanium carbide, tantalum carbide, zirconium carbide, hafnium carbide, Ti6/4, silicon carbide, chrome carbide, vanadium carbide, yttria stabilized zirconia, magnesia stabilized zirconia, zirconia toughened alumina, titanium molybdenum hafnium, alloys including one or more of the above metals, ceramics, quartz, garnet, sapphire, combinations of these materials, combinations of these and other materials, and other materials may also be used for a desired nozzle or component.

Sintered Polycrystalline Diamond Compacts

One useful material for manufacturing nozzle surfaces, however, is a sintered polycrystalline diamond compact due to its superior performance. Diamond has the greatest hardness and the lowest coefficient of friction of any currently known material. Sintered polycrystalline diamond compacts are chemically inert, are impervious to all solvents, and have the highest thermal conductivity at room temperature of any known material.

In some embodiments of the devices, a polycrystalline diamond compact provides unique chemical bonding and mechanical grip between the diamond and the substrate material.

A method by which PDC may be manufactured is described later in this document. Briefly, it involves sintering diamond crystals to each other, and to a substrate under high pressure and high temperature. FIGS. 1A and 1B illustrate the physical and chemical processes involved manufacturing polycrystalline diamond compacts.

In FIG. 1A, a quantity of diamond feedstock 130 (such as diamond powder or crystals) is placed adjacent to a metal-containing substrate 110 prior to sintering. In the region of the diamond feedstock 130, individual diamond crystals 131 may be seen, and between the individual diamond crystals 131 there are interstitial spaces 132. If desired, a quantity of solvent-catalyst metal may be placed into the interstitial spaces 132. The substrate may also contain solvent-catalyst metal.

The substrate 110 may be a suitable pure metal or alloy, or a cemented carbide containing a suitable metal or alloy as a cementing agent such as cobalt-cemented tungsten carbide. The substrate may be a metal with high tensile strength. In a cobalt-chrome substrate of the devices, the cobalt-chrome alloy will serve as a solvent-catalyst metal for solvating diamond crystals during the sintering process.

The illustration shows the individual diamond crystals and the contiguous metal crystals in the metal substrate. The interface 120 between diamond powder and substrate material is a critical region where bonding of the diamond table to the substrate must occur. In some embodiments of the devices, a boundary layer of a third material different than the diamond and the substrate is placed at the interface 120. This interface boundary layer material, when present, may serve several functions including, but not limited to, enhancing the bond of the diamond table to the substrate, and mitigation of the residual stress field at the diamond-substrate interface.

Once diamond powder or crystals and substrate are assembled as shown in FIG. 1A, the assembly is subjected to high pressure and high temperature as described later herein in order to cause bonding of diamond crystals to diamond crystals and to the substrate. The resulting structure of sintered polycrystalline diamond table bonded to a substrate is called a pqlycrystalline diamond compact (PDC). A compact, as the term is used herein, is a composite structure of two different materials, such as diamond crystals, and a substrate metal. The analogous structure incorporating cubic boron nitride crystals in the sintering process instead of diamond crystals is called polycrystalline cubic boron nitride compact (PCBNC). Many of the processes described herein for the fabrication and finishing of PDC structures and parts work in a similar fashion for PCBNC. In some embodiments of the devices, PCBNC may be substituted for PDC.

FIG. 1B depicts a polycrystalline diamond compact 101 after the high pressure and high temperature sintering of diamond feedstock to a substrate. Within the PDC structure, there is an identifiable volume of substrate 102, an identifiable volume of diamond table 103, and a transition zone 104 between diamond table and substrate containing diamond crystals and substrate material. Crystalline grains of substrate material 105 and sintered crystals of diamond 106 are depicted.

On casual examination, the finished compact of FIG. 1B will appear to consist of a solid table of diamond 103 attached to the substrate 402 with a discrete boundary. On very close examination, however, a transition zone 104 between diamond table 103 and substrate 102 can be characterized. This zone represents a gradient interface between diamond table and substrate with a gradual transition of ratios between diamond content and metal content. At the substrate side of the transition zone, there will be only a small percentage of diamond crystals and a high percentage of substrate metal, and on the diamond table side, there will be a high percentage of diamond crystals and a low percentage of substrate metal. Because of this gradual transition of ratios of polycrystalline diamond to substrate metal in the transition zone, the diamond table and the substrate have a gradient interface.

In the transition zone or gradient transition zone where diamond crystals and substrate metal are intermingled, chemical bonds are formed between the diamond and metal. From the transition zone 104 into the diamond table 103, the metal content diminishes and is limited to solvent-catalyst metal that fills the three-dimensional vein-like structure of interstitial voids, openings or asperities 107 within the sintered diamond table structure 103. The solvent-catalyst metal found in the voids or openings 107 may have been swept up from the substrate during sintering or may have been solvent-catalyst metal added to the diamond feedstock before sintering.

During the sintering process, there are three types of chemical bonds that are created: diamond-to-diamond bonds, diamond-to-metal bonds, and metal-to-metal bonds. In the diamond table, there are diamond-to-diamond bonds (sp3 carbon bonds) created when diamond particles partially solvate in the solvate-catalyst metal and then are bonded together. In the substrate and in the diamond table, there are metal-to-metal bonds created by the high pressure and high temperature sintering process. And in the gradient transition zone, diamond-to-metal bonds are created between diamond and solvent-catalyst metal.

The combination of these various chemical bonds and the mechanical grip exerted by solvent-catalyst metal in the diamond table such as in the interstitial spaces of the diamond structure diamond table provide extraordinarily high bond strength between the diamond table and the substrate. Interstitial spaces are present in the diamond structure and those spaces typically are filled with solvent-catalyst metal, forming veins of solvent-catalyst metal within the polycrystalline diamond structure. This bonding structure contributes to the extraordinary fracture toughness of the compact, and the veins of metal within the diamond table act as energy sinks halting propagation of incipient cracks within the diamond structure. The transition zone and metal vein structure provide the compact with a gradient of material properties between those of the diamond table and those of substrate material, further contributing to the extreme toughness of the compact. The transition zone can also be called an interface, a gradient transition zone, a composition gradient zone, or a composition gradient, depending on its characteristics. The transition zone distributes diamond/substrate stress over the thickness of the zone, reducing zone high stress of a distinct linear interface. The subject residual stress is created as pressure and temperature are reduced at the conclusion of the high pressure/high temperature sintering process due to the difference in pressure and thermal expansive properties of the diamond and substrate materials.

The diamond sintering process occurs under conditions of extremely high pressure and high temperature. According to the inventors' best experimental and theoretical understanding, the diamond sintering process progresses through the following sequence of events. At pressure, a cell containing feedstock of unbonded diamond powder or crystals (diamond feedstock) and a substrate is heated to a temperature above the melting point of the substrate metal 110 and molten metal flows or sweeps into the interstitial voids 107 between the adjacent diamond crystals 106. It is carried by the pressure gradient to fill the voids as well as being pulled in by the surface energy or capillary action of the large surface area of the diamond crystals 106. As the temperature continues to rise, carbon atoms from the surface of diamond crystals dissolve into this interstitial molten metal, forming a carbon solution.

At the proper threshold of temperature and pressure, diamond becomes the thermodynamically favored crystalline allotrope of carbon. As the solution becomes super saturated with respect to C_(d) (carbon diamond), carbon from this solution begins to crystallize as diamond onto the surfaces of diamond crystals bonding adjacent diamond crystals together with diamond-diamond bonds into a sintered polycrystalline diamond structure 106. The interstitial metal fills the remaining void space forming the vein-like lattice structure 107 within the diamond table by capillary forces and pressure driving forces. Because of the crucial role that the interstitial metal plays in forming a solution of carbon atoms and stabilizing these reactive atoms during the diamond crystallization phase in which the polycrystalline diamond structure is formed, the metal is referred to as a solvent-catalyst metal.

FIG. 1BB depicts a sintered polycrystalline diamond compact having both substrate metal 180 and diamond 181, but in which there is a continuous gradient transition 182 from substrate metal to diamond. In such a compact, the gradient transition zone may be the entire compact, or a portion of the compact. The substrate side of the compact may contain nearly pure metal for easy machining and attachment to other components, while the diamond side may be extremely hard, smooth and durable for use in a hostile work environment.

In some embodiments of the devices, a quantity of solvent-catalyst metal may be combined with the diamond feedstock prior to sintering. This is found to be useful when forming thick PCD tables, solid PDC structures, or when using multimodal fine diamond where there is little residual free space within the diamond powder. In each of these cases, there may not be sufficient ingress of solvent-catalyst metal via the sweep mechanism to adequately mediate the sintering process as a solvent-catalyst. The metal may be added by direct addition of powder, or by generation of metal powder in situ with an attritor mill or by the well-known method of chemical reduction of metal salts deposited on diamond crystals. Added metal may constitute any amount from less than 1% by mass, to greater than 35%. This added metal may consist of the same metal or alloy as is found in the substrate, or may be a different metal or alloy selected because of its material and mechanical properties. Example ratios of diamond feedstock to solvent-catalyst metal prior to sintering include mass ratios of 70:30, 85:15, 90:10, and 95:15. The metal in the diamond feedstock may be added powder metal, metal added by an attritor method, vapor deposition or chemical reduction of metal into powder.

When sintering diamond on a substrate with an interface boundary layer, it may be that no solvent-catalyst metal from the substrate is available to sweep into the diamond table and participate in the sintering process. In this case, the boundary layer material, if composed of a suitable material, metal or alloy that can function as a solvent-catalyst, may serve as the sweep material mediating the diamond sintering process. In other cases where the desired boundary material cannot serve as a solvent-catalyst, a suitable amount of solvent-catalyst metal powder as described herein is added to the diamond crystal feed stock as described above. This assembly is then taken through the sintering process. In the absence of a substrate metal source, the solvent-catalyst metal for the diamond sintering process must be supplied entirely from the added metal powder. The boundary material may bond chemically to the substrate material, and bonds chemically to the diamond table and/or the added solvent-catalyst metal in the diamond table. The remainder of the sintering and fabrication process may be the same as with the conventional solvent-catalyst sweep sintering and fabrication process.

For the sake of simplicity and clarity in this patent, the substrate, transition zone, and diamond table have been discussed as distinct layers. However, it is important to realize that the finished sintered object may be a composite structure characterized by a continuous gradient transition from substrate material to diamond table rather than as distinct layers with clear and discrete boundaries, hence the term “compact”.

In addition to the sintering processes described above, diamond parts suitable for use as nozzles components may also be fabricated as solid or free-standing polycrystalline diamond structures without a substrate. These may be formed by placing the diamond powder combined with a suitable amount of added solvent-catalyst metal powder as described above in a refractory metal can (typically Ta, Nb, Zr, or Mo) with a shape approximating the shape of the final part desired. This assembly is then taken through the sintering process. However, in the absence of a substrate metal source, the solvent-catalyst metal for the diamond sintering process must be supplied entirely from the added metal powder. With suitable finishing, objects thus formed may be used as is, or bonded to metal or other substrates.

Sintering is a method of creating a diamond table with a strong and durable constitution. Other methods of producing a diamond table that may or may not be bonded to a substrate are possible. At present, these typically are not as strong or durable as those fabricated with the sintering process. It is also possible to use these methods to form diamond structures directly onto substrates suitable for use as nozzles. A table of polycrystalline diamond either with or without a substrate may be manufactured and later attached to a nozzle in a location such that it will form a surface. The attachment could be performed with any suitable method, including welding, brazing, sintering, diffusion welding, diffusion bonding, inertial welding, adhesive bonding, or the use of fasteners such as screws, bolts, or rivets. In the case of attaching a diamond table without a substrate to another object, the use of such methods as brazing, diffusion welding/bonding or inertia welding may be most appropriate.

Although high pressure/high temperature sintering is a method for creating a diamond surface, other methods for producing a volume of diamond may be employed as well. For example, either chemical vapor deposition (CVD), or physical vapor deposition (PVD) processes may be used. CVD produces a diamond layer by thermally cracking an organic molecule and depositing carbon radicals on a substrate. PVD produces a diamond layer by electrically causing carbon radicals to be ejected from a source material and to deposit on a substrate where they build a diamond crystal structure.

The CVD and PVD processes have some advantages over sintering. Sintering is performed in large, expensive presses at high pressure (such as 45-68 kilobars) and at high temperatures (such as 1200 to 1500 degrees Celsius). It is difficult to achieve and maintain desired component shape using a sintering process because of flow of high pressure mediums used and possible deformation of substrate materials.

In contrast, CVD and PVD take place at atmospheric pressure or lower, so there no need for a pressure medium and there is no deformation of substrates.

Another disadvantage of sintering is that it is difficult to achieve some geometries in a sintered polycrystalline diamond compact. When CVD or PVD are used, however, the gas phase used for carbon radical deposition can completely conform to the shape of the object being coated, making it easy to achieve a desired non-planar shape.

Another potential disadvantage of sintering polycrystalline diamond compacts is that the finished component will tend to have large residual stresses caused by differences in the coefficient of thermal expansion and modulus between the diamond and the substrate. While residual stresses can be used to improve strength of a part, they can also be disadvantageous. When CVD or PVD is used, residual stresses can be minimized because CVD and PVD processes do not involve a significant pressure transition (such from 68 Kbar to atmospheric pressure in high pressure and high temperature sintering) during manufacturing.

Another potential disadvantage of sintering polycrystalline diamond compacts is that few substrates have been found that are suitable for sintering. Tungsten carbide is a common choice for substrate materials. When CVD or PVD are used, however, synthetic diamond can be placed on many substrates, including titanium, most carbides, silicon, molybdenum and others. This is because the temperature and pressure of the CVD and PVD coating processes are low enough that differences in coefficient of thermal expansion and modulus between diamond and the substrate are not as critical as they are in a high temperature and high pressure sintering process.

A further difficulty in manufacturing sintered polycrystalline diamond compacts is that as the size of the part to be manufactured increases, the size of the press must increase as well. Sintering of diamond will only take place at certain pressures and temperatures, such as those described herein. In order to manufacture larger sintered polycrystalline diamond compacts, ram pressure of the press (tonnage) and size of tooling (such as dies and anvils) must be increased in order to achieve the necessary pressure for sintering to take place. But increasing the size and capacity of a press is more difficult than simply increasing the dimensions of its components. There may be a practical physical size constraints on press size due to the manufacturing process used to produce press tooling.

Tooling for a press is typically made from cemented tungsten carbide. In order to make tooling, the cemented tungsten carbide is sintered in a vacuum furnace followed by pressing in a hot isosatic press (“HIP”) apparatus. Hipping must be performed in a manner that maintains uniform temperature throughout the tungsten carbide in order to achieve uniform physical qualities and quality. These requirements impose a practical limit on the size tooling that can be produced for a press that is useful for sintering polycrystalline diamond compacts. The limit on the size tooling that can be produced also limits the size press that can be produced.

CVD and PVD manufacturing apparatuses may be scaled up in size with few limitations, allowing them to produce polycrystalline diamond compacts of almost any desired size.

CVD and PVD processes are also advantageous because they permit precise control of the thickness and uniformity of the diamond coating to be applied to a substrate. Temperature is adjusted within the range of 500 to 1000 degrees Celsius, and pressure is adjusted in a range of less than 1 atmosphere to achieve desired diamond coating thickness.

Another advantage of CVD and PVD processes is that they allow the manufacturing process to be monitored as it progresses. A CVD or PVD reactor can be opened before manufacture of a part is completed so that the thickness and quality of the diamond coating being applied to the part may be determined. From the thickness of the diamond coating that has already been applied, time to completion of manufacture can be calculated. Alternatively, if the coating is not of desired quality, the manufacturing processes may be aborted in order to save time and money.

In contrast, sintering of polycrystalline diamond compacts is performed as a batch process that cannot be interrupted, and progress of sintering cannot be monitored. The pressing process must be run to completion and the part may only be examined afterward.

CVD and PVD Diamond

CVD is performed in an apparatus called a reactor. A basic CVD reactor includes four components. The first component of the reactor is one or more gas inlets. Gas inlets may be chosen based on whether gases are premixed before introduction to the chamber or whether the gases are allowed to mix for the first time in the chamber. The second component of the reactor is one or more power sources for the generation of thermal energy. A power source is needed to heat the gases in the chamber. A second power source may be used to heat the substrate material uniformly in order to achieve a uniform coating of diamond on the substrate. The third component of the reactor is a stage or platform on which a substrate is placed. The substrate will be coated with diamond during the CVD process. Stages used include a fixed stage, a translating stage, a rotating stage and a vibratory stage. An appropriate stage must be chosen to achieved desired diamond coating quality and uniformity. The fourth component of the reactor is an exit port for removing exhaust gas from the chamber. After gas has reacted with the substrate, it must be removed from the chamber as quickly as possible so that it does not participate in other reactions, which would be deleterious to the diamond coating.

CVD reactors are classified according to the power source used. The power source is chosen to create the desired species necessary to carry out diamond thin film deposition. Some CVD reactor types include plasma-assisted microwave, hot filament, electron beam, single, double or multiple laser beam, arc jet and DC discharge. These reactors differ in the way they impart thermal energy to the gas species and in their efficiency in breaking gases down to the species necessary for deposition of diamond. It is possible to have an array of lasers to perform local heating inside a high pressure cell. Alternatively, an array of optical fibers could be used to deliver light into the cell.

The basic process by which CVD reactors work is as follows. A substrate is placed into the reactor chamber. Reactants are introduced to the chamber via one or more gas inlets. For diamond CVD, methane (CH₄) and hydrogen (H₂) gases may be brought into the chamber in premixed form. Instead of methane, any carbon-bearing gas in which the carbon has sp3 bonding may be used. Other gases may be added to the gas stream in order to control quality of the diamond film, deposition temperature, gain structure and growth rate. These include oxygen, carbon dioxide, argon, halogens and others.

The gas pressure in the chamber may be maintained at about 100 torr. Flow rates for the gases through the chamber may be about 10 standard cubic centimeters per minute for methane and about 100 standard cubic centimeters per minute for hydrogen. The composition of the gas phase in the chamber may be in the range of 90-99.5% hydrogen and 0.5-10% methane.

When the gases are introduced into the chamber, they are heated. Heating may be accomplished by many methods. In a plasma-assisted process, the gases are heated by passing them through a plasma. Otherwise, the gases may be passed over a series of wires such as those found in a hot filament reactor.

Heating the methane and hydrogen will break them down into various free radicals. Through a complicated mixture of reactions, carbon is deposited on the substrate and joins with other carbon to form crystalline diamond by sp3 bonding. The atomic hydrogen in the chamber reacts with and removes hydrogen atoms from methyl radicals attached to the substrate surface in order to create molecular hydrogen, leaving a clear solid surface for further deposition of free radicals.

If the substrate surface promotes the formation of sp2 carbon bonds, or if the gas composition, flow rates, substrate temperature or other variables are incorrect, then graphite rather than diamond will grow on the substrate.

There are many similarities between CVD reactors and processes and PVD reactors and processes. PVD reactors differ from CVD reactors in the way that they generate the deposition species and in the physical characteristics of the deposition species. In a PVD reactor, a plate of source material is used as a thermal source, rather than having a separate thermal source as in CVD reactors. A PVD reactor generates electrical bias across a plate of source material in order to generate and eject carbon radicals from the source material. The reactor bombards the source material with high energy ions. When the high energy ions collide with source material, they cause ejection of the desired carbon radicals from the source material. The carbon radicals are ejected radially from the source material into the chamber. The carbon radicals then deposit themselves onto whatever is in their path, including the stage, the reactor itself, and the substrate.

Referring to FIG. 1C, a substrate 140 of appropriate material is depicted having a deposition face 141 on which diamond may be deposited by a CVD or PVD process. FIG. 1D depicts the substrate 140 and the deposition face 141 on which a volume of diamond 142 has been deposited by CVD or PVD processes. A small transition zone 143 is present in which both diamond and substrate are located. In comparison to FIG. 1B, it can be seen that the CVD or PVD diamond deposited on a substrate lacks the more extensive gradient transition zone of sintered polycrystalline diamond compacts because there is no sweep of solvent-catalyst metal through the diamond table in a CVD or PVD process.

Both CVD and PVD processes achieve diamond deposition by line of sight. Means (such as vibration and rotation) are provided for exposing all desired surfaces for diamond deposition. If a vibratory stage is to be used, the surface will vibrate up and down with the stage and thereby present all surfaces to the free radical source.

There are several methods, which may be implemented in order to coat cylindrical objects with diamond using CVD or PVD processes. If a plasma assisted microwave process is to be used to achieve diamond deposition, then the object to receive the diamond must be directly under the plasma in order to achieve the highest quality and most uniform coating of diamond. A rotating or translational stage may be used to present every aspect of the surface to the plasma for diamond coating. As the stage rotates or translates, all portions of the surface may be brought directly under the plasma for coating in such a way to achieve sufficiently uniform coating.

If a hot filament CVD process is used, then the surface should be placed on a stationary stage. Wires or filaments (typically tungsten) are strung over the stage so that their coverage includes the surface to be coated. The distance between the filaments and the surface and the distance between the filaments themselves may be chosen to achieve a uniform coating of diamond directly under the filaments.

Diamond surfaces can be manufactured by CVD and PVD process either by coating a substrate with diamond or by creating a free standing volume of diamond, which is later mounted for use. A free standing volume of diamond may be created by CVD and PVD processes in a two-step operation. First, a thick film of diamond is deposited on a suitable substrate, such as silicon, molybdenum, tungsten or others. Second, the diamond film is released from the substrate.

As desired, segments of diamond film may be cut away, such as by use of a Q-switched YAG laser. Although diamond is transparent to a YAG laser, there is usually a sufficient amount of sp2 bonded carbon (as found in graphite) to allow cutting to take place. If not, then a line may be drawn on the diamond film using a carbon-based ink. The line should be sufficient to permit cutting to start, and once started, cutting will proceed slowly.

After an appropriately-sized piece of diamond has been cut from a diamond film, it can be attached to a desired object in order to serve as a surface. For example, the diamond may be attached to a substrate by welding, diffusion bonding, adhesion bonding, mechanical fixation or high pressure and high temperature bonding in a press.

Although CVD and PVD diamond on a substrate do not exhibit a gradient transition zone that is found in sintered polycrystalline diamond compacts, CVD and PVD process can be conducted in order to incorporate metal into the diamond table. As mentioned elsewhere herein, incorporation of metal into the diamond table enhances adhesion of the diamond table to its substrate and can strengthen the polycrystalline diamond compact. Incorporation of diamond into the diamond table can be used to achieve a diamond table with a coefficient of thermal expansion and compressibility different from that of pure diamond, and consequently increasing fracture toughness of the diamond table as compared to pure diamond. Diamond has a low coefficient of thermal expansion and a low compressibility compared to metals. Therefore the presence of metal with diamond in the diamond table achieves a higher and more metal-like coefficient of thermal expansion and the average compressibility for the diamond table than for pure diamond. Consequently, residual stresses at the interface of the diamond table and the substrate are reduced, and delamination of the diamond table from the substrate is less likely.

A pure diamond crystal also has low fracture toughness. Therefore, in pure diamond, when a small crack is formed, the entire diamond component fails catastrophically. In comparison, metals have a high fracture toughness and can accommodate large cracks without catastrophic failure. Incorporation of metal into the diamond table achieves a greater fracture toughness than pure diamond. In a diamond table having interstitial spaces and metal within those interstitial spaces, if a crack forms in the diamond and propagates to an interstitial space containing metal, the crack will terminate at the metal and catastrophic failure will be avoided. Because of this characteristic, a diamond table with metal in its interstitial spaces is able to sustain much higher forces and workloads without catastrophic failure compared to pure diamond.

Diamond-diamond bonding tends to decrease as metal content in the diamond table increases. CVD and PVD processes can be conducted so that a transition zone is established. However, the surface can be essentially pure polycrystalline diamond for low wear properties.

Generally CVD and PVD diamond is formed without large interstitial spaces filled with metal. Consequently, most PVD and CVD diamond is more brittle or has a lower fracture toughness than sintered polycrystalline diamond compacts. CVD and PVD diamond may also exhibit the maximum residual stresses possible between the diamond table and the substrate. It is possible, however, to form CVD and PVD diamond film that has metal incorporated into it with either a uniform or a functionally gradient composition.

One method for incorporating metal into a CVD or PVD diamond film it to use two different source materials in order to simultaneously deposit the two materials on a substrate in a CVD of PVD diamond production process. This method may be used regardless of whether diamond is being produced by CVD, PVD or a combination of the two.

Another method for incorporating metal into a CVD diamond film chemical vapor infiltration. This process would first create a porous layer of material, and then fill the pores by chemical vapor infiltration. The porous layer thickness should be approximately equal to the desired thickness for either the uniform or gradient layer. The size and distribution of the pores can be sued to control ultimate composition of the layer. Deposition in vapor infiltration occurs first at the interface between the porous layer and the substrate. As deposition continues, the interface along which the material is deposited moves outward from the substrate to fill pores in the porous layer. As the growth interface moves outward, the deposition temperature along the interface is maintained by moving the sample relative to a heater or by moving the heater relative to the growth interface. It is imperative that the porous region between the outside of the sample and the growth interface be maintained at a temperature that does not promote deposition of material (either the pore-filling material or undesired reaction products). Deposition in this region would close the pores prematurely and prevent infiltration and deposition of the desired material in inner pores. The result would be a substrate with open porosity and poor physical properties.

Laser Deposition of Diamond

Another alternative manufacturing process that may be used to produce surfaces and components of the devices involves use of energy beams, such as laser energy, to vaporize constituents in a substrate and redeposit those constituents on the substrate in a new form, such as in the form of a diamond coating. As an example, a metal, polymeric or other substrate may be obtained or produced containing carbon, carbides or other desired constituent elements. Appropriate energy, such as laser energy, may be directed at the substrate to cause constituent elements to move from within the substrate to the surface of the substrate adjacent the area of application of energy to the substrate. Continued application of energy to the concentrated constituent elements on the surface of the substrate can be used to cause vaporization of some of those constituent elements. The vaporized constituents may then be reacted with another element to change the properties and structure of the vaporized constituent elements.

Next, the vaporized and reacted constituent elements (which may be diamond) may be diffused into the surface of the substrate. A separate fabricated coating may be produced on the surface of the substrate having the same or a different chemical composition than that of the vaporized and reacted constituent elements. Alternatively, some of the changed constituent elements which were diffused into the substrate may be vaporized and reacted again and deposited as a coating on the. By this process and variations of it, appropriate coatings such as diamond, cubic boron nitride, diamond like carbon, B₄C, SiC, TiC, TiN, TiB, cCN, Cr₃C₂, and Si₃N₄ may be formed on a substrate.

In other manufacturing environments, high temperature laser application, electroplating, sputtering, energetic laser excited plasma deposition or other methods may be used to place a volume of diamond, diamond-like material, a hard material or a superhard material in a location in which will serve as a surface.

In light of the disclosure herein, those of ordinary skill in the art will comprehend the apparatuses, materials and process conditions necessary for the formation and use of high quality diamond on a substrate using any of the manufacturing methods described herein in order to create a diamond surface.

Material Property Considerations

There is a particular problem posed by the manufacture of a non-planar diamond surface. The non-planar component design requires that pressures be applied radially in making the part. During the high pressure sintering process, described in detail below, all displacements must be along a radian emanating from the center of the part that will be produced in order to achieve the desired non-planar geometry. To achieve this in high temperature/high pressure pressing, an isostatic pressure field must be created. During the manufacture of such non-planar parts, if there is any deviatoric stress component, it will result in distortion of the part and may render the manufactured part useless.

Special considerations that must be taken into account in making non-planar polycrystalline diamond compacts are discussed below.

Modulus

Most polycrystalline diamond compacts include both a diamond table and a substrate. The material properties of the diamond and the substrate may be compatible, but the high pressure and high temperature sintering process in the formation of a polycrystalline diamond compact may result in a component with excessively high residual stresses. For example, for a polycrystalline diamond compact using tungsten carbide as the substrate, the sintered diamond has a Young's modulus of approximately 120 million p.s.i., and cobalt cemented tungsten carbide has a modulus of approximately 90 million p.s.i. Modulus refers to the slope of the curve of the stress plotted against the stress for a material. Modulus indicates the stiffness of the material. Bulk modulus refers to the ratio of isostatic strain to isostatic stress, or the unit volume reduction of a material versus the applied pressure or stress.

Because diamond and most substrate materials have such a high modulus, a very small stress or displacement of the polycrystalline diamond compact can induce very large stresses. If the stresses exceed the yield strength of either the diamond or the substrate, the component will fail. The strongest polycrystalline diamond compact is not necessarily stress free. In a sintered polycrystalline diamond compact with optimal distribution of residual stress, more energy is required to induce a fracture than in a stress free component. Thus, the difference in modulus between the substrate and the diamond must be noted and used to design a component that will have the best strength for its application with sufficient abrasion resistance and fracture toughness.

Coefficient of Thermal Expansion (CTE)

The extent to which diamond and its substrate differ in how they deform relative to changes in temperature also affects their mechanical compatibility. Coefficient of thermal expansion (“CTE”) is a measure of the unit change of a dimension with unit change in temperature or the propensity of a material to expand under heat or to contract when cooled. As a material experiences a phase change, calculations based on CTE in the initial phase will not be applicable. It is notable that when compacts of materials with different CTE's and moduluses are used, they will stress differently at the same stress.

Polycrystalline diamond has a coefficient of thermal expansion (as above and hereafter referred to as “CTE” on the order of 2-4 micro inches per inch (10⁻⁶ inches) of material per degree (in/in° C.). In contrast, carbide has a CTE on the order of 6-8-in/in° C. Although these values appear to be close numerically, the influence of the high modulus creates very high residual stress fields when a temperature gradient of a few hundred degrees is imposed upon the combination of substrate and diamond. The difference in coefficient of thermal expansion is less of a problem in simple planarl polycrystalline diamond compacts than in the manufacture of non-planar or complex shapes. When a non-planar polycrystalline diamond compact is manufactured, differences in the CTE between the diamond and the substrate can cause high residual stress with subsequent cracking and failure of the diamond table, the substrate or both at any time during or after high pressure/high temperature sintering.

Dilatoric and Deviatoric Stresses

The diamond and substrate assembly will experience a reduction of free volume during the sintering process. The sintering process, described in detail below, involves subjecting the substrate and diamond assembly to pressure ordinarily in the range of about 40 to about 68 kilobar. The pressure will cause volume reduction of the substrate. Some geometrical distortion of the diamond and/or the substrate may also occur. The stress that causes geometrical distortion is called deviatoric stress, and the stress that causes a change in volume is called dilatoric stress. In an isostatic system, the deviatoric stresses sum to zero and only the dilatoric stress component remains. Failure to consider all of these stress factors in designing and sintering a polycrystalline diamond component with complex geometry (such as concave and convex non-planar polycrystalline diamond compacts) will likely result in failure of the process.

Free Volume Reduction of Diamond Feedstock

As a consequence of the physical nature of the feedstock diamond, large amounts of free volume are present unless special preparation of the feedstock is undertaken prior to sintering. It is necessary to eliminate as much of the free volume in the diamond as possible, and if the free volume present in the diamond feedstock is too great, then sintering may not occur. It is also possible to eliminate the free volume during sintering if a press with sufficient ram displacement is employed. Is important to maintain a desired uniform geometry of the diamond and substrate during any process which reduces free volume in the feedstock, or a distorted or faulty component may result.

Selection of Solvent-Catalyst Metal

Formation of synthetic diamond in a high temperature and high pressure press without the use of a solvent-catalyst metal is not a viable method at this time, although it may become viable in the future. A solvent-catalyst metal is at this time required to achieve desired crystal formation in synthetic diamond. The solvent-catalyst metal first solvates carbon preferentially from the sharp contact points of the diamond feedstock crystals. It then recrystallizes the carbon as diamond in the interstices of the diamond matrix with diamond-diamond bonding sufficient to achieve a solid with 95 to 97% of theoretical density with solvent metal 5-3% by volume. That solid distributed over the substrate surface is referred to herein as a polycrystalline diamond table. The solvent-catalyst metal also enhances the formation of chemical bonds with substrate atoms.

A method for adding the solvent-catalyst metal to diamond feedstock is by causing it to sweep from the substrate that contains solvent-catalyst metal during high pressure and high temperature sintering. Powdered solvent-catalyst metal may also be added to the diamond feedstock before sintering, particularly if thicker diamond tables are desired. An attritor method may also be used to add the solvent-catalyst metal to diamond feedstock before sintering. If too much or too little solvent-catalyst metal is used, then the resulting part may lack the desired mechanical properties, so it is important to select an amount of solvent-catalyst metal and a method for adding it to diamond feedstock that is appropriate for the particular part to be manufactured.

Diamond Feedstock Particle Size and Distribution

The durability of the finished diamond product is integrally linked to the size of the feedstock diamond and also to the particle distribution. Selection of the proper size(s) of diamond feedstock and particle distribution depends upon the service requirement of the specimen and also its working environment. The durability of polycrystalline diamond is enhanced if smaller diamond feedstock crystals are used and a highly diamond-diamond bonded diamond table is achieved.

Although polycrystalline diamond may be made from single modal diamond feedstock, use of multi-modal feedstock increases both impact strength and wear resistance. The use of a combination of large crystal sizes and small crystal sizes of diamond feedstock together provides a part with high impact strength and wear resistance, in part because the interstitial spaces between the large diamond crystals may be filled with small diamond crystals. During sintering, the small crystals will solvate and reprecipitate in a manner that binds all of the diamond crystals into a strong and tightly bonded compact.

Diamond Feedstock Loading Methodology

Contamination of the diamond feedstock before or during loading will cause failure of the sintering process. Great care must be taken to ensure the cleanliness of diamond feedstock and any added solvent-catalyst metal or binder before sintering.

In order to prepare for sintering, clean diamond feedstock, substrate, and container components are prepared for loading. The diamond feedstock and the substrate are placed into a refractory metal container called a “can” which will seal its contents from outside contamination. The diamond feedstock and the substrate will remain in the can while undergoing high pressure and high temperature sintering in order to form a polycrystalline diamond compact. The can may be sealed by electron beam welding at high temperature and in a vacuum.

Enough diamond aggregate (powder or grit) is loaded to account for linear shrinkage during high pressure and high temperature sintering. The method used for loading diamond feedstock into a can for sintering affects the general shape and tolerances of the final part. In particular, the packing density of the feedstock diamond throughout the can should be as uniform as possible in order to produce a good quality sintered polycrystalline diamond compact structure. In loading, bridging of diamond can be avoided by staged addition and packing.

The degree of uniformity in the density of the feedstock material after loading will affect geometry of the polycrystalline diamond compact. Loading of the feedstock diamond in a dry form versus loading diamond combined with a binder and the subsequent process applied for the removal of the binder will also affect the characteristics of the finished polycrystalline diamond compact. In order to properly pre-compact diamond for sintering, the pre-compaction pressures should be applied under isostatic conditions.

Selection of Substrate Material

The unique material properties of diamond and its relative differences in modulus and CTE compared to most potential substrate materials diamond make selection of an appropriate polycrystalline diamond substrate a formidable task. A great disparity in material properties between the diamond and the substrate creates challenges successful manufacture of a polycrystalline diamond component with the needed strength and durability. Even very hard substrates appear to be soft compared to polycrystalline diamond. The substrate and the diamond must be able to withstand not only the pressure and temperature of sintering, but must be able to return to room temperature and atmospheric pressure without delaminating, cracking or otherwise failing.

Selection of substrate material also requires consideration of the intended application for the part, impact resistance and strengths required, and the amount of solvent-catalyst metal that will be incorporated into the diamond table during sintering. Substrate materials must be selected with material properties that are compatible with those of the diamond table to be formed.

Substrate Geometry

Further, it is important to consider whether to use a substrate which has a smooth surface or a surface with topographical features. Substrate surfaces may be formed with a variety of topographical features so that the diamond table is fixed to the substrate with both a chemical bond and a mechanical grip. Use of topographical features on the substrate provides a greater surface area for chemical bonds and with the mechanical grip provided by the topographical features, can result in a stronger and more durable component.

Example Materials and Manufacturing Steps

The inventors have discovered and determined materials and manufacturing processes for constructing polycrystalline diamond compacts for use in a nozzle. It is also possible to manufacture the invented surfaces by methods and using materials other than those listed below.

The steps described below, such as selection of substrate material and geometry, selection of diamond feedstock, loading and sintering methods, will affect each other, so although they are listed as separate steps that must be taken to manufacture a polycrystalline diamond compact, no step is completely independent of the others, and all steps must be standardized to ensure success of the manufacturing process.

Select Substrate and/or Solvent-Catalyst Metal

In order to manufacture any polycrystalline diamond component, an appropriate substrate should be selected. For the manufacture of a polycrystalline diamond component to be used in a nozzle, various substrates may be used as desired. TABLE 2 SOME SUBSTRATES FOR NOZZLE APPLICATIONS SUBSTRATE ALLOY NAME REMARKS Titanium Ti6/4 (TiAlVa) A thin tantalum ASTM F-1313 barrier may be (TiNbZr) placed on the ASTM F-620 titanium substrate ASTM F-1580 before loading TiMbHf diamond feedstock. Nitinol (TiNi + other) Cobalt chrome ASTM F-799 Contains cobalt, chromium and molybdenum. Wrought product Cobalt chrome ASTM F-90 Contains cobalt, chromium, tungsten and nickel. Cobalt chrome ASTM F-75 Contains cobalt, chromium and molybdenum. Cast product. Cobalt chrome ASTM F-562 Contains cobalt, chromium, molybdenum and nickel. Cobalt chrome ASTM F-563 Contains cobalt, chromium, molybdenum, tungsten, iron and nickel. Tantalum ASTM F-560 refractory metal. (unalloyed) Platinum various Niobium ASTM F-67 refractory metal. (unalloyed) Maganese Various May include Cr, Ni, Mg, molybdenum. Cobalt cemented WC Commonly used in tungsten carbide synthetic diamond production Cobalt chrome CoCr cemented cemented WC tungsten carbide Cobalt chrome CoCr cemented cemented CrC chrome carbide Cobalt chrome CoCr cemented cemented SiC silicon carbide Fused silicon carbide SiC Cobalt chrome CoCrMo A thin tungsten or molybdenum tungsten/cobalt layer may be placed on the substrate before loading diamond feedstock. Stainless steel Various The CoCr used may be either CoCrMo or CoCrW. The preceding substrates are examples only. In addition to these substrates, other materials may be appropriate for use as substrates for construction of nozzle s and other surfaces.

When titanium is used as the substrate, sometimes place a thin tantalum barrier layer is placed on the titanium substrate. The tantalum barrier prevents mixing of the titanium alloys with cobalt alloys used in the diamond feedstock. If the titanium alloys and the cobalt alloys mix, it possible that a detrimentally low melting point eutectic inter-metallic compound will be formed during the high pressure and high temperature sintering process. The tantalum barrier bonds to both the titanium and cobalt alloys, and to the polycrystalline diamond that contains cobalt solvent-catalyst metals. Thus, a polycrystalline diamond compact made using a titanium substrate with a tantalum barrier layer and diamond feedstock that has cobalt solvent-catalyst metals can be very strong and well formed. Alternatively, the titanium substrate may be provided with an alpha case oxide coating (an oxidation layer) forming a barrier which prevents formation of a eutectic metal.

If a cobalt chrome molybdenum substrate is used, a thin tungsten layer or a thin tungsten and cobalt layer can be placed on the substrate before loading of the diamond feedstock in order to control formation of chrome carbide (CrC) during sintering.

In addition to those listed, other appropriate substrates may be used for forming polycrystalline diamond compact surfaces. Further, it is possible within the scope of the devices to form a diamond surface for use without a substrate. It is also possible to form a surface from any of the superhard materials and other materials listed herein, in which case a substrate may not be needed. Additionally, if it is desired to use a type of diamond or carbon other than polycrystalline diamond, substrate selection may differ. For example, if a diamond surface is to be created by use of chemical vapor deposition or physical vapor deposition, then use of a substrate appropriate for those manufacturing environments and for the compositions used will be necessary.

Determination of Substrate Geometry

A substrate geometry appropriate for the compact to be manufactured and appropriate for the materials being used should be selected. In order to manufacture a non-planar diamond surface, it is necessary to select a substrate geometry that will facilitate the manufacture of those parts. In order to ensure proper diamond formation and avoid compact distortion, forces acting on the diamond and the substrate during sintering must be strictly radial. Therefore the substrate geometry at the contact surface with diamond feedstock for manufacturing a complex surface in some instances may be generally non-planar.

As mentioned previously, there is a great disparity in the material characteristics of synthetic diamond and most available substrate materials. In particular, modulus and CTE are of concern. But when applied in combination with each other, some substrates can form a stable and strong polycrystalline diamond compact. The table below lists physical properties of some substrate materials. TABLE 3 MATERIAL PROPERTIES OF SOME EXAMPLE SUBSTRATES SUBSTRATE MATERIAL MODULUS CTE Ti 6/4 16.5 million psi 5.4 CoCrMo 35.5 million psi 16.9 CoCrW 35.3 million psi 16.3 Use of either titanium or cobalt chrome substrates alone for the manufacture of non-planar polycrystalline diamond compacts may result in cracking of the diamond table or separation of the substrate from the diamond table. In particular, it appears that titanium's dominant property during high pressure and high temperature sintering is compressibility while cobalt chrome's dominant property during sintering is CTE. In some embodiments of the devices, a substrate of two or more layers may be used in order to achieve dimensional stability during and after manufacturing.

In various embodiments of the devices, a single layer substrate may be utilized. In other embodiments of the devices, a two-layer substrate may be utilized, as discussed. Depending on the properties of the components being used, however, it may be desired to utilize a substrate that includes three, four or more layers. Such multi-layer substrates are intended to be comprehended within the scope of the devices.

Substrate Surface Topography

Depending on the application, it may be advantageous to include substrate surface topographical features on a substrate that is to be formed into a polycrystalline diamond compact. Regardless whether a one-piece, a two-piece of a multi-piece substrate is used, it may be desirable to modify the surface of the substrate or provide topographical features on the substrate in order to increase the total surface area of diamond to enhance substrate to diamond contact and to provide a mechanical grip of the diamond table.

The placement of topographical features on a substrate serves to modify the substrate surface geometry or contours from what the substrate surface geometry or contours would be if formed as a simple planar or non-planar figure. Substrate surface topographical features may include one or more different types of topographical features which result in protruding, indented or contoured features that serve to increase surface, mechanically interlock the diamond table to the substrate, prevent crack formation, or prevent crack propagation.

Substrate surface topographical features or substrate surface modifications serve a variety of useful functions. Use of substrate topographical features increases total substrate surface area of contact between the substrate and the diamond table. This increased surface area of contact between diamond table and substrate results in a greater total number of chemical bonds between diamond table and substrate than if the substrate surface topographical features were absent, thus achieving a stronger polycrystalline diamond compact.

Substrate surface topographical features also serve to create a mechanical interlock between the substrate and the diamond table. The mechanical interlock is achieved by the nature of the substrate topographical features and also enhances strength of the polycrystalline diamond compact.

Substrate surface topographical features may also be used to distribute the residual stress field of the polycrystalline diamond compact over a larger surface area and over a larger volume of diamond and substrate material. This greater distribution can be used to keep stresses below the threshold for crack initiation and/or crack propagation at the diamond table/substrate interface, within the diamond itself and within the substrate itself.

Substrate surface topographical features increase the depth of the gradient interface or transition zone between diamond table and substrate, in order to distribute the residual stress field through a longer segment of the composite compact structure and to achieve a stronger part.

Substrate surface modifications can be used to created a sintered polycrystalline diamond compact that has residual stresses that fortify the strength of the diamond layer and yield a more robust polycrystalline diamond compact with greater resistance to breakage than if no surface topographical features were used. This is because in order to break the diamond layer, it is necessary to first overcome the residual stresses in the part and then overcome the strength of the diamond table.

Substrate surface topographical features redistribute forces received by the diamond table. Substrate surface topographical features cause a force transmitted through the diamond layer to be re-transmitted from single force vector along multiple force vectors. This redistribution of forces travelling to the substrate avoids conditions that would deform the substrate material at a more rapid rate than the diamond table, as such differences in deformation can cause cracking and failure of the diamond table.

Substrate surface topographical features may be used to mitigate the intensity of the stress field between the diamond and the substrate in order to achieve a stronger part.

Substrate surface topographical features may be used to distribute the residual stress field throughout the polycrystalline diamond compact structure in order to reduce the stress per unit volume of structure.

Substrate surface topographical features may be used to mechanically interlock the diamond table to the substrate by causing the substrate to compress over an edge of the diamond table during manufacturing. Dovetailed, heminon-planar and lentate modifications act to provide force vectors that tend to compress and enhance the interface of diamond table and substrate during cooling as the substrate dilitates radially.

Substrate surface topographical features may also be used to achieve a manufacturable form. As mentioned herein, differences in coefficient of thermal expansion and modulus between diamond and the chosen substrate may result in failure of the polycrystalline diamond compact during manufacturing. For certain parts, the stronger interface between substrate and diamond table that may be achieved when substrate topographical features are used can achieve a polycrystalline diamond compact that can be successfully manufactured. But if a similar part of the same dimensions is to be made using a substrate with a simple substrate surface rather than specialized substrate surface topographical features, the diamond table may crack or separate from the substrate due to differences in coefficient of thermal expansion or modulus of the diamond and the substrate.

Examples of useful substrate surface topographical features include waves, grooves, ridges, other longitudinal surface features (any of which may be arranged longitudinally, lattitudinally, crossing each other at a desired angle, in random pattems, and in geometric patterns), three dimensional textures, non-planar segment depressions, non-planar segment protrusions, triangular depressions, triangular protrusions, arcuate depressions, arcuate protrusions, partially non-planar depressions, partially non-planar protrusions, cylindrical depressions, cylindrical protrusions, rectangular depressions, rectangular protrusions, depressions of n-sided polygonal shapes where n is an integer, protrusions of n-sided polygonal shapes, a waffle pattern of ridges, a waffle iron pattern of protruding structures, dimples, nipples, protrusions, ribs, fenestrations, grooves, troughs or ridges that have a cross-sectional shape that is rounded, triangular, arcuate, square, polygonal, curved, or otherwise, or other shapes. Machining, pressing, extrusion, punching, injection molding and other manufacturing techniques for creating such forms may be used to achieve desired substrate topography. Although for illustration purposes, some sharp corners are depicted on substrate topography or other structures in the drawings, in practice it is expected that all corners will have a small radius to achieve a component with superior durability.

Although many substrate topographies have been depicted in convex non-planar substrates, those surface topographies may be applied to convex non-planar substrate surfaces, other non-planar substrate surfaces, and flat substrate surfaces. Substrate surface topographies which are variations or modifications of those shown, and other substrate topographies which increase component strength or durability may also be used.

Diamond Feedstock Selection

It is anticipated that typically the diamond particles used will be in the range of less than 1 micron to more than 100 microns. In some embodiments of the devices, however, diamond particles as small as 1 nanometer may be used. Smaller diamond particles are used for smoother surfaces. Commonly, diamond particle sizes will be in the range of 0.5 to 2.0 microns or 0.1 to 10 microns.

An example diamond feedstock is shown in the table below. TABLE 4 EXAMPLE BIMODAL DIAMOND FEEDSTOCK MATERIAL AMOUNT 4 to 8 micron diamond about 90% 0.5 to 1.0 micron diamond about 9% Titanium carbonitride powder about 1% This formulation mixes some smaller and some larger diamond crystals so that during sintering, the small crystals may dissolve and then recrystallize in order to form a lattice structure with the larger diamond crystals. Titanium carbonitride powder may optionally be included in the diamond feedstock in order to prevent excessive diamond grain growth during sintering in order to produce a finished product that has smaller diamond crystals.

Another diamond feedstock example is provided in the table below. TABLE 5 EXAMPLE TRIIMODAL DIAMOND FEEDSTOCK MATERIAL AMOUNT Size x diamond crystals about 90% Size 0.1x diamond crystals about 9% Size 0.01x diamond crystals about 1% The trimodal diamond feedstock described above can be used with any suitable diamond feedstock having a first size or diameter “x”, a second size 0.1× and a third size 0.1×. This ratio of diamond crystals allows packing of the feedstock to about 89% theoretical density, closing most interstitial spaces and providing the densest diamond table in the finished polycrystalline diamond compact.

Another diamond feedstock example is provided in the table below. TABLE 6 EXAMPLE TRIIMODAL DIAMOND FEEDSTOCK MATERIAL AMOUNT Size x diamond crystals about 88-92% Size 0.1x diamond crystals about 8-12% Size 0.01x diamond crystals about 0.8-1.2%

Another diamond feedstock example is provided in the table below. TABLE 7 EXAMPLE TRIIMODAL DIAMOND FEEDSTOCK MATERIAL AMOUNT Size x diamond crystals about 85-95% Size 0.1x diamond crystals about 5-15% Size 0.01x diamond crystals about 0.5-1.5%

Another diamond feedstock example is provided in the table below. TABLE 8 EXAMPLE TRIIMODAL DIAMOND FEEDSTOCK MATERIAL AMOUNT Size x diamond crystals about 80-90% Size 0.1x diamond crystals about 10-20% Size 0.01x diamond crystals about 0-2%

In some embodiments of the devices, the diamond feedstock used will be diamond powder having a greatest dimension of about 100 nanometers or less. In some embodiments of the devices some solvent-catalyst metal is included with the diamond feedstock to aid in the sintering process, although in many applications there will be a significant solvent-catalyst metal sweep from the substrate during sintering as well.

Solvent Metal Selection

It has already been mentioned that solvent metal will sweep from the substrate through the diamond feedstock during sintering in order to solvate some diamond crystals so that they may later recrystallize and form a diamond-diamond bonded lattice network that characterizes polycrystalline diamond. It is possible to include some solvent-catalyst metal in the diamond feedstock only when required to supplement the sweep of solvent-catalyst metal from the substrate.

Traditionally, cobalt, nickel and iron have been used as solvent metals for making polycrystalline diamond. Platinum and other materials could also be used for a binder.

CoCr may be used as a solvent-catalyst metal for sintering PCD to achieve a more wear resistant PDC. Infiltrating diamond particles with Cobalt (Co) metal produces standard polycrystalline diamond compact. As the cobalt infiltrates the diamond, carbon is dissolved (mainly from the smaller diamond grains) and reprecipitates onto the larger diamond grains causing the grains to grow together. This is known as liquid phase sintering. The remaining pore spaces between the diamond grains are filled with cobalt metal.

In this example, the alloy Cobalt Chrome (CoCr) may be used as the solvent metal which acts similarly to Co metal. However, it differs in that the CoCr reacts with some of the dissolved carbon resulting in the precipitation of CoCr carbides. These carbides, like most carbides, are harder (abrasion resistant) than cobalt metal and results in a more wear or abrasion resistant PDC.

Other metals can be added to Co to form metal carbides as precipitates within the pore spaces between the diamond grains. These metals include the following, but not limited to, Ti, W, Mo, V, Ta, Nb, Zr, Si, and combinations thereof.

It is important not just to add the solvent metal to diamond feedstock, but also to include solvent metal in an appropriate proportion and to mix it evenly with the feedstock. The use of about 86% diamond feedstock and 15% solvent metal by mass (weight) has provided good result, other useful ratios of diamond feedstock to solvent metal may include 5:95, 10:90, 20:80, 30:70, 40:60, 50:50, 60:40, 65:35, 75:25, 80:20, 90:10, 95:5, 97:3, 98:2, 99:1, 99.5:0.5, 99.7:0.3, 99.8:0.2, 99.9:0.1 and others.

In order to mix the diamond feedstock with solvent-catalyst metal, first the amounts of feedstock and solvent metal to be mixed may be placed together in a mixing bowl, such as a mixing bowl made of the desired solvent-catalyst metal. Then the combination of feedstock and solvent metal may be mixed at an appropriate speed (such as 200 rpm) with dry methanol and attritor balls for an appropriate time period, such as 30 minutes. The attritor balls, the mixing fixture and the mixing bowl may be made from the solvent-catalyst metal. The methanol may then be decanted and the diamond feedstock separated from the attritor balls. The feedstock may then be dried and cleaned by firing in a molecular hydrogen furnace at about 1000 degrees Celsius for about 1 hour. The feedstock is then ready for loading and sintering. Alternatively, it may be stored in conditions which will preserve its cleanliness. Appropriate furnaces which may be used for firing also include hydrogen plasma furnaces and vacuum furnaces.

Loading Diamond Feedstock

Referring to FIG. 3, an apparatus for carrying out a loading technique is depicted. The apparatus includes a spinning rod 301 with a longitudinal axis 302, the spinning rod being capable of spinning about its longitudinal axis. The spinning rod 701 has an end 303 matched to the size and shape of the part to be manufactured. For example, if the part to be manufactured is non-planar, the spinning rod end 303 may be heminon-planar.

A compression ring 304 is provided with a bore 305 through which the spinning rod 301 may project. A die 306 or can is provided with a cavity 307 also matched to the size and shape of the part to be made.

In order to load diamond feedstock, the spinning rod is placed into a drill chuck and the spinning rod is aligned with the center point of the die. The depth to which the spinning rod stops in relation to the cavity of the die is controlled with a set screw and monitored with a dial indicator.

The die is charged with a known amount of diamond feedstock material. The spinning rod is then spun about its longitudinal axis and lowered into the die cavity to a predetermined depth. The spinning rod contacts and rearranges the diamond feedstock during this operation. Then the spinning of the spinning rod is stopped and the spinning rod is locked in place.

The compression ring is then lowered around the outside of the spinning rod to a point where the compression ring contacts diamond feedstock in the cavity of the die. The part of the compression ring that contacts the diamond is annular. The compression ring is tamped up and down to compact the diamond. This type of compaction is used to distribute diamond material throughout the cavity to the same density and may be done in stages to prevent bridging. Packing the diamond with the compaction ring causes the density of the diamond around the equator of the sample caused to be very uniform and the same as that of the polar region in the cavity. In this configuration, the diamond sinters in a truly non-planar fashion and the resulting part maintains its sphericity to close tolerances.

Binding Diamond Feedstock Generally

Another method which may be employed to maintain a uniform density of the feedstock diamond is the use of a binder. A binder is added to the correct volume of feedstock diamond, and then the combination is pressed into a can. Some binders which might be used include polyvinyl butyryl, polymethyl methacrylate, polyvinyl formol, polyvinyl chloride acetate, polyethylene, ethyl cellulose, methylabietate, paraffin wax, polypropylene carbonate and polyethyl methacrylate.

In one embodiment of the devices, the process of binding diamond feedstock includes four steps. First, a binder solution is prepared. A binder solution may be prepared by adding about 5 to 25% plasticizer to pellets of poly(propylene carbonate), and dissolving this mixture in solvent such as 2-butanone to make about a 20% solution by weight.

Plasticizers that may be used include nonaqueous binders generally, glycol, dibutyl phthalate, benzyl butyl phthalate, alkyl benzyl phthalate, diethylhexyl phthalate, diisoecyl phthalate, diisononyl phthalate, dimethyl phthalate, dipropylene glycol dibenzoate, mixed glycols dibenzoate, 2-ethylhexyl diphenyl dibenzoate, mixed glycols dibenzoate, 2-ethylhexyl diphenyl phosphate, isodecyl diphenyl phosphate, isodecyl diphenl phosphate, tricrestyl phosphate, tributoxy ethyl phosphate, dihexyl adipate, triisooctyl trimellitate, dioctyl phthalate, epoxidized linseed oil, epoxidized soybean oil, acetyl triethyl citrate, propylene carbonate, various phthalate esters, butyl stearate, glycerin, polyalkyl glycol derivatives, diethyl oxalate, paraffin wax and triethylene glycol. Other appropriate plasticizers may be used as well.

Solvents that may be used include 2-butanone, methylene chloride, chloroform, 1,2-dichloroethne, trichlorethylene, methyl acetate, ethyl acetate, vinyl acetate, propylene carbonate, n-propyl acetate, acetonitrile, dimethylformamide, propionitrile, n-mehyl-2-pyrrolidene, glacial acetic acid, dimethyl sulfoxide, acetone, methyl ethyl ketone, cyclohexanone, oxysolve 80a, caprotactone, butyrolactone, tetrahydrofuran, 1,4 dioxane, propylene oxide, cellosolve acetate, 2-methoxy ethyl ether, benzene, styrene, xylene, ethanol, methanol, toluene, cyclohexane, chlorinated hydrocarbons, esters, ketones, ethers, ethyl benzene and various hydrocarbons. Other appropriate solvents may be used as well.

Second, diamond is mixed with the binder solution. Diamond may be added to the binder solution to achieve about a 2-25% binder solution (the percentage is calculated without regard to the 2-butanone).

Third, the mixture of diamond and binder solution is dried. This may be accomplished by placing the diamond and binder solution mixture in a vacuum oven for about 24 hours at about 50 degrees Celsius in order to drive out all of the solvent 2-butanone. Fourth, the diamond and binder may be pressed into shape. When the diamond and binder is removed from the oven, it will be in a clump that may be broken into pieces which are then pressed into the desired shape with a compaction press. A pressing spindle of the desired geometry may be contacted with the bound diamond to form it into a desired shape. When the diamond and binder have been pressed, the spindle is retracted. The final density of diamond and binder after pressing may be at least about 2.6 grams per cubic centimeter.

If a volatile binder is used, it should be removed from the shaped diamond prior to sintering. The shaped diamond is placed into a furnace and the binding agent is either gasified or pyrolized for a sufficient length of time such that there is no binder remaining. Polycrystalline diamond compact quality is reduced by foreign contamination of the diamond or substrate, and great care must be taken to ensure that contaminants and binder are removed during the furnace cycle. Ramp up and the time and temperature combination are critical for effective pyrolization of the binder. For the binder example given above, the debinding process that may be used to remove the binder is as follows. Reviewing FIG. 4 while reading this description may be helpful.

First, the shaped diamond and binder are heated to from ambient temperature to about 500 degrees Celsius. The temperature may be increased by about 2 degrees Celsius per minute until about 500 degrees Celsius is reached. Second, the temperature of the bound and shaped diamond is maintained at about 500 degrees Celsius for about 2 hours. Third, the temperature of the diamond is increased again. The temperature may be increased from about 500 degrees Celsius by about 4 degrees per minute until a temperature of about 950 degrees Celsius is reached. Fourth, the diamond is maintained at about 950 degrees Celsius for about 6 hours. Fifth, the diamond is then permitted to return to ambient temperature at a temperature decrease of about 2 degrees per minute.

In some embodiments of the devices, it may be desirable to preform bound diamond feedstock by an appropriate process, such as injection molding. The diamond feedstock may include diamond crystals of one or more sizes, solvent-catalyst metal, and other ingredients to control diamond recrystallization and solvent-catalyst metal distribution. Handling the diamond feedstock is not difficult when the desired final curvature of the part is flat, convex dome or conical. However, when the desired final curvature of the part has complex contours, such as illustrated herein, providing uniform thickness and accuracy of contours of the polycrystalline diamond compact is more difficult when using powder diamond feedstock. In such cases it may be desirable to perform the diamond feedstock before sintering.

If it is desired to perform diamond feedstock prior to loading into a can for sintering, rather than placing powder diamond feedstock into the can, the steps described herein and variations of them may be followed. First, as already described, a suitable binder is added to the diamond feedstock. Optionally, powdered solvent-catalyst metal and other components may be added to the feedstock as well. The binder will typically be a polymer chosen for certain characteristics, such as melting point, solubility in various solvents, and CTE. One or more polymers may be included in the binder. The binder may also include an elastomer and/or solvents as desired in order to achieve desired binding, fluid flow and injection molding characteristics. The working volume of the binder to be added to a feedstock may be equal to or slightly more than the measured volume of empty space in a quantity of lightly compressed powder. Since binders typically consist of materials such as organic polymers with relatively high CTE's, the working volume should be calculated for the injection molding temperatures expected. The binder and feedstock should be mixed thoroughly to assure uniformity of composition. When heated, the binder and feedstock will have sufficient fluid character to flow in high pressure injection molding. The heated feedstock and binder mixture is then injected under pressure into molds of desired shape. The molded part then cools in the mold until set, and the mold can then be opened and the part removed. Depending on the final polycrystalline diamond compact geometry desired, one or more molded diamond feedstock component can be created and placed into a can for polycrystalline diamond compact sintering. Further, use of this method permits diamond feedstock to be molded into a desired form and then stored for long periods of time prior to use in the sintering process, thereby simplifying manufacturing and resulting in more efficient production.

As desired, the binder may be removed from the injection molded diamond feedstock form. A variety of methods are available to achieve this. For example, by simple vacuum or hydrogen furnace treatment, the binder may be removed from the diamond feedstock form. In such a method, the form would be brought up to a desired temperature in a vacuum or in a very low pressure hydrogen (reducing) environment. The binder will then volatilize with increasing temperature and will be removed from the form. The form may then be removed from the furnace. When hydrogen is used, it helps to maintain extremely clean and chemically active surfaces on the diamond crystals of the diamond feedstock form.

An alternative method for removing the binder from the form involves utilizing two or polymer (such as polyethylene) binders with different molecular weights. After initial injection molding, the diamond feedstock form is placed in a solvent bath which removes the lower molecular weight polymer, leaving the higher molecular weight polymer to maintain the shape of the diamond feedstock form. Then the diamond feedstock form is placed in a furnace for vacuum or very low pressure hydrogen treatment for removal of the higher molecular weight polymer.

Partial or complete binder removal from the diamond feedstock form may be performed prior to assembly of the form in a pressure assembly for polycrystalline diamond compact sintering. Alternatively, the pressure assembly including the diamond feedstock form may be placed into a furnace for vacuum or very low pressure hydrogen furnace treatment and binder removal.

Dilute Binder

In some embodiments, dilute binder may be added to PCD, PCBN or ceramic powders to hold form. This technique may be used to provide an improved method of forming Polycrystalline Diamond Compact (PDC), Polycrystalline Cubic Boron Nitride (PCBN), ceramic, or cermet powders into layers of various geometries. A PDC, PCBN, ceramic or cermet powder may be mixed with a temporary organic binder. This mixture may be mixed and cast or calendared into a sheet (tape) of the desired thickness. The sheet may be dried to remove water or organic solvents. The dried tape may be then cut into shapes needed to conform to the geometry of a corresponding substrate. The tape/substrate assembly may be then heated in a vacuum furnace to drive off the binder material. The temperature may be then raised to a level where the ceramic or cermet powder fuses to itself and/or to the substrate, thereby producing a uniform continuous ceramic or cermet coating bonded to the substrate.

Referring to FIG. 5, a die 55 with a cup/can in it 54 and diamond feedstock against it 52 are depicted. A punch 53 is used to form the diamond feedstock into a desired shape. Binder liquid 51 is not added to the powder until after the diamond, PCBN, ceramic or cermet powder 52 is in the preferred geometry. Dry powder 52 is spin formed using a rotating formed punch 53 in a refectory containment can 54 supported in a holding die 55. In another method shown in FIG. 6, feedstock powder 62 is added to a mold 66. A punch forms the feedstock to shape. A vibrator 67 may be used help the powder 62 take on the shape of the mold 66. After the powder feedstock is in the desired geometry, a dilute solution of an organic binder with a solvent is allowed to percolate through the powder granules.

As shown in FIGS. 7 and 8, one powder layer 88 can be loaded, and after a few minutes, when the binder is cured sufficiently at room temperature, another layer 89 can be loaded on top of the first layer 88. This method is particularly useful in producing PDC or CBN with multiple layers of varying powder particle size and metal content. The process can be repeated to produce as many layers as desired. FIG. 7 shows a section view of a spherical, multi-layered powder load using a first layer 88, second layer 89, third layer 810, and final layer 811. The binder content should be kept to minimum to produce good loading density and to limit the amount of gas produced during the binder removal phase to reduce the tendency of the containment cans being displaced from a build up of internal pressure.

Once all of the powder layers are loaded the binder may be burned-out in a vacuum oven at a vacuum of about 200 Militorrs or less and at the time and desired temperature profile, such as that shown in FIG. 9. An acceptable binder is 0.5 to 5% propylene carbonate in methyl ethyl keytone.

Gradients

Diamond feedstock may be selected and loaded in order to create different types of gradients in the diamond table. These include an interface gradient diamond table, an incremental gradient diamond table, and a continuous gradient diamond table.

If a single type or mix of diamond feedstock is loaded adjacent a substrate, as discussed elsewhere herein, sweep of solvent-catalyst metal through the diamond will create an interface gradient in the gradient transition zone of the diamond table.

An incremental gradient diamond table may be created by loading diamond feedstocks of differing characteristics (diamond particle size, diamond particle distribution, metal content, etc.) in different strata or layers before sintering. For example, a substrate is selected, and a first diamond feedstock containing 60% solvent-catalyst metal by weight is loaded in a first strata adjacent the substrate. Then a second diamond feedstock containing 40% solvent-catalyst metal by weight is loaded in a second strata adjacent the first strata. Optionally, additional strata of diamond feedstock may be used. For example, a third strata of diamond feedstock containing 20% solvent-catalyst metal by weight may be loaded adjacent the second strata.

A continuous gradient diamond table may be created by loading diamond feedstock in a manner that one or more of its characteristics continuously vary from one depth in the diamond table to another. For example, diamond particle size may vary from large near a substrate (in order to create large interstitial spaces in the diamond for solvent-catalyst metal to sweep into) to small near the diamond surface in order to create a part that is strongly bonded to the substrate but that has a very low friction surface.

The diamond feedstocks of the different strata may be of the same or different diamond particle size and distribution. Solvent-catalyst metal may be included in the diamond feedstock of the different strata in weight percentages of from about 0% to more than about 80%. In some embodiments, diamond feedstock will be loaded with no solvent-catalyst metal in it, relying on sweep of solvent-catalyst metal from the substrate to achieve sintering. Use of a plurality of diamond feedstock strata, the strata having different diamond particle size and distribution, different solvent-catalyst metal by weight, or both, allows a diamond table to be made that has different physical characteristics at the interface with the substrate than at the surface. This allows a polycrystalline diamond compact to be manufactured which has a diamond table very firmly bonded to its substrate.

Bisquing Processes to Hold Shapes

If desired, a bisquing process may be used to hold shapes for subsequent processing of polycrystalline diamond compacts, polycrystalline cubic boron nitride, and ceramic or cermet products. This involves an interim processing step in High Temperature High Pressure (HTHP) sintering of Polycrystalline Diamond Compact (PDC), Polycrystalline Boron Nitride (PCBN), ceramic, or cermet powders called “bisquing.” Bisquing may provide the following enhancements to the processing of the above products:

-   -   a. Pre-sintered shapes can be controlled that are at a certain         density and size.     -   b. Product consistency is improved dramatically.     -   c. Shapes can be handled easily in the bisque form.     -   d. In layered constructs, bisquing keeps the different layers         from contaminating each other.     -   e. Bisquing different components or layers separately increase         the separation of work elements increasing production efficiency         and quality.     -   f. Bisquing molds are often easer to handle and manage prior to         final assembly that the smaller final product forms.

Bisquing molds or containers can be fabricated from any high temperature material that has a melting point higher than the highest melting point of any mix component to be bisque. Bisque mold/container materials that work well are Graphite, Quartz, Solid Hexagonal Boron Nitride (HBN), and ceramics. Some refractory type metals (High temperature stainless steels, Nb, W, Ta, Mo, etc) work well is some applications where bisquing temperatures are lower and sticking of the bisque powder mix is not a problem. Molds or containers can be shaped by pressing, forming, or machining, and are preferably polished at the interface between the bisque material and the mold/container itself. Some mold/container materials glazing and/or firing prior to use.

FIG. 10 shows an embodiment 1006 for making a cylinder with a concave relief or trough using the bisquing process. Pre-mixed powders of PDC, PCBN, ceramic, or cermet materials 1001 which contain enough metal to undergo solid phase sintering are loaded into the bisquing molds or containers 1002 and 1004. A release agent may be required between the mold/container to ensure that the final bisque form can be removed following furnace firing. Some release agents that may be used are HBN, Graphite, Mica, and Diamond Powder. A bisque mold/container lid with an integral support form 1005 is placed over the loaded powder material to ensure that the material holds form during the sintering process. The bisque mold/container assembly is then placed in a hydrogen atmosphere furnace, or alternately, in a vacuum furnace which is drawn to a vacuum ranging from 200 to 0 Militorrs. The load is then heated within a range of 0.6 to 0.8 of the melting temperature of the largest volume mix metal. A typical furnace cycle is shown in FIG. 12. Once the furnace cycle is completed and the mold/container is cooled, the hardened bisque formed powders can be removed for further HPHT processing. A bisque form of feedstock 1003 is the net product.

FIG. 11 shows fabrication 1110 of a bisque form for a full hemispherical part 1109 that has multiple powder layers 1107 a and 1107 b. Pre-mixed powders of PDC, PCBN, ceramic, or cermet materials which contain enough metal to undergo solid phase sintering are loaded into the bisquing molds or containers. A release agent may be required between the mold/container to ensure that the final bisque form can be removed following furnace firing. The bisque mold/container assembly may then placed in a vacuum furnace which is drawn to a vacuum ranging from 200 to 0 Militorrs. The load is then heated within a range of 0.6 to 0.8 of the melting temperature of the largest volume mix metal. Once the furnace cycle is completed and the mold/container is cooled, the hardened bisque 1109 formed powders can be removed for further HPHT processing.

Reduction of Free Volume in Diamond Feedstock

As mentioned earlier, it may be desirable to remove free volume in the diamond feedstock before sintering is attempted. This may be a useful procedure especially when producing non-planar concave and convex parts. If a press with sufficient anvil travel is used for high pressure and high temperature sintering, however, this step may not be necessary. Free volume in the diamond feedstock may in some instances be reduced so that the resulting diamond feedstock is at least about 95% theoretical density and sometimes closer to about 97% of theoretical density.

Referring to FIGS. 13 and 14, an assembly used for precompressing diamond to eliminate free volume is depicted. In the drawing, the diamond feedstock is intended to be used to make a convex non-planar polycrystalline diamond part. The assembly may be adapted for precompressing diamond feedstock for making polycyrstalline diamond compacts of other complex shapes.

The assembly depicted includes a cube 1301 of a pressure transfer medium. A cube is made from pyrophillite or other appropriate pressure transfer material such as a synthetic pressure medium and is intended to undergo pressure from a cubic press with anvils simultaneously pressing the six faces of the cube. A cylindrical cell rather than a cube would be used if a belt press were utilized for this step.

The cube 801 has a cylindrical cavity 1302 or passage through it. The center of the cavity 1302 will receive a non-planar refractory metal can 1310 loaded with diamond feedstock 806 that is to be precompressed. The diamond feedstock 1306 may have a substrate with it.

The can 1310 consists of two heminon-planar can halves 1310 a and 1310 b, one of which overlaps the other to form a slight lip 1312. The can may be an appropriate refractory metal such as niobium, tantalum, molybdenum, etc. The can is typically two hemispheres, one which is slightly larger to accept the other being slid inside of it to fully enclosed the diamond feedstock. A rebated area or lip is provided in the larger can so that the smaller can will satisfactorily fit therein. The seam of the can is sealed with an appropriate sealant such as dry hexagonal boronitride or a synthetic compression medium. The sealant forms a barrier that prevents the salt pressure medium from penetrating the can. The can seam may also be welded by plasma, laser, or electron beam processes.

An appropriately shaped pair of salt domes 1304 and 1307 surround the can 1310 containing the diamond feedstock 1306. In the example shown, the salt domes each have a heminon-planar cavity 1305 and 1308 for receiving the can 1310 containing the non-planar diamond feedstock 1306. The salt domes and the can and diamond feedstock are assembled together so that the salt domes encase the diamond feedstock. A pair of cylindrical salt disks 1303 and 1309 are assembled on the exterior of the salt domes 1304 and 1307. All of the aforementioned components fit within the bore 1302 of the pressure medium cube 1301.

The entire pyrocube assembly is placed into a press and pressurized under appropriate pressure (such as about 40-68 Kbar) and for an appropriate although brief duration to precompress the diamond and prepare it for sintering. No heat is necessary for this step.

Mold Releases

When making non-planar shapes, it may be desirable to use a mold in the sintering process to produce the desired net shape. CoCr metal may used as a mold release in forming shaped diamond or other superhard products. Sintering the superhard powder feed stocks to a substrate, the object of which is to lend support to the resulting superhard table, may be utilized to produce standard Polycrystalline Diamond Compact (PDC) and Polycrystalline Cubic Boron Nitride (PCBN) parts. However, in some applications, it is desired to remove the diamond table from the substrate.

Referring to FIG. 14, a diamond layer 1402 and 1403 has been sintered to a substrate 1401 at an interface 1404. The interface 1404 must be broken to result in free standing diamond if the substrate is not required in the final product. A mold release may be used to remove the substrate from the diamond table. If CoCr alloy is used for the substrate, then the CoCr itself serves as a mold release, as well as serving as a solvent-catalyst metal. CoCr works well as a mold release because its Coefficient of Thermal Expansion (CTE) is dramatically different than that of sintered PDC or PCBN 3. Because of the large disparity in the CTE's between PDC and PCBN and CoCr, high stress is formed at the interface 1501 between these two materials as shown in FIG. 15. The stress that is formed is greater than the bond energy between the two materials. When the stress is greater than the bond energy, a crack is formed at the point of highest stress. The crack then propagates following the narrow region of high stress concentrated at the interface. Referring to FIG. 16, in this way, the CoCr substrate 1601 will separate from the PCD or PCBN 1602 that was sintered around it, regardless of the shape of the interface.

Materials other than CoCr can be used as a mold release. These materials include those metals with high CTE's and, in particular, those that are not good carbide formers. These are, for example, Co, Ni, CoCr, CoFe, CoNi, Fe, steel, etc.

Gradient Layers and Stress Modifiers

Gradient layers and stress modifiers may be used in the making of superhard constructs. Gradient layers may be used to achieve any of the following objectives:

-   -   a. Improve the “sweep” of solvent metal into the outer layer of         superhard material and to control the amount of solvent metal         introduced for sintering into said outer layer.     -   b. Provide a “sweep” source to flush out impurities for deposit         on the surface of the outer layer of superhard material and/or         chemical attachment/combination with the refractory containment         cans.     -   c. Control the Bulk Modulus of the various gradient layers and         thereby control the overall dilatation of the construct during         the sintering process.     -   d. Affect the “Coefficient of Thermal Expansion” (CTE) of each         of the various layers by changing the ratio of metal or carbides         to diamond, PCBN or other Superhard materials to reduce the CTE         of an individual gradient layer.     -   e. Allow for the control of structural stress fields through the         various levels of gradient layers to optimize the overall         construct.     -   f. Change the direction of stress tensors to improve the outer         Superhard layer, e.g., direct the tensor vectors toward the         center of a spherical construct to place the outer layer diamond         into compression, or conversely, direct the tensor vectors from         the center of the construct to reduce interface stresses between         the various gradient layers.     -   g. Improve the overall structural stress compliance to external         or internal loads by providing a construct that has         substantially reduced brittleness and increased toughness         wherein loads are transferred through the construct without         crack initiation and propagation.

Referring to FIG. 17, The liquid sintering phase of Polycrystalline Diamond (PDC) and Polycrystalline Cubic Boron Nitride (PCBN) is typically accomplished by mixing the solvent sintering metal 1701 directly with the Diamond or PCBN powders 1702 prior to the “High Temperature High Pressure (HPHT) pressing, or (referring to FIG. 18) “sweeping” the solvent metal 1802 from a substrate 1801 into feedstock powders from the adjacent substrate during HPHT. The very best high quality PDC or PCBN is created using the “sweep” process.

There are several theories related to the increased PDC and CBH quality when using the sweep method. However, most of those familiar with the field agree that allowing the sintering metal to “sweep” from the substrate material provides a “wave front” of sintering metal that quickly “wets” and dissolves the diamond or CBN and uses only as much metal as required to precipitate Diamond or PCBN particle-to-particle bonding. Whereas in a “prerriixed” environment the metal “blinds off” the particle-to particle reaction because too much metal is present, or conversely, not enough metal is present to ensure the optimal reaction.

Furthermore, it is felt that the “wave front” of metal sweeping through the powder matrix also carries away impurities that would otherwise impede the formation of high quality PDC of PCBN. These impurities are normally “pushed” ahead of the sintering metal “wave front” and are deposited in pools adjacent to the refractory containment cans. FIG. 19 depicts the substrate 1904, the wavefront 1903, and the feedstock crystals or powder 1902 which the wavefront will sweep through 1901. Certain refractory material such as Niobium, Molybdenum, and Zirconium can act as “getters” which combine with the impurities as they immerge from the matrix giving additional assistance in the creation of high quality end products.

While there are compelling reasons to use the “sweep” process in sintering PDC and PCBN there are also problems that arise out of its use. For example, not all substrate metals are as controllable as others as to the quantity of material that is delivered and ultimately utilized by the powder matrix during sintering. Cobalt metal (6 to 13% by volume) sweeping from cemented tungsten carbide is very controllable when used against diamond or PCBN powders ranging from 1 to 40 microns particle sized. On the other hand, Cobalt Chrome Molybdenum (CoCrMo) that is useful as a solvent metal to make PDC for some applications overwhelms the same PDC matrix with CoCrMo metal in a pure sweep process sometimes producing inferior quality PDC. The fact that the CoCrMo has a lower melting point than cobalt, and further that there is an inexhaustible supply when using a solid CoCrMo substrate adjacent to the PDC matrix, creates a non-controllable processing condition.

In some applications where it is necessary to use sintering metals such a CoCrMo that can not be “swept” from a cemented carbide product, it is necessary to provide a simulated substrate against the PDC powders that provides a controlled release and limited supply of CoCrMo for the process.

These “simulated” substrates have been developed in the forms of “gradient” layers of mixtures of diamond, carbides, and metals to produce the desired “sweep” affect for sintering the outer layer of PDC. The first “gradient layer” (just adjacent to the outer or primary diamond layer which will act as the bearing or wear surface) can be prepared using a mixture of Diamond, Cr₃C₂, and CoCrMo. Depending of the size fraction of the diamond powder used in the outer layer, the first gradient layers diamond size fraction and metal content is adjusted for the optimal sintering conditions.

Where a “simulated” substrate is used, it has been discovered that often a small amount of solvent metal, in this case CoCrMo must be added to the outside diamond layer as catalyst to “kick-off” the sintering reaction.

One embodiment utilizes the mix ranges for the outer 2001 and inner 2002 gradient layers of FIG. 20 that are listed in Table 9. TABLE 9 DIAMOND DIAMOND Cr₃C₂ CoCrMo GRADIENT (Vol. (Size (Vol. (Vol. LAYERS Percent) Fraction-μm) Percent) Percent) Outer 92 25 0 8 Inner 70 40 10 20

The use of gradient layers with solid layers of metal allows the designer to match the Bulk Modulus to the Coefficient of Thermal Expansion (CTE) of various features of the construct to counteract dilatory forces encountered during the HTHP phase of the sintering process. For example, in a spherical construct as the pressure increases the metals in the construct are compressed or dilated radially toward the center of the sphere. Conversely, as the sintering temperature increases the metal expands radially away from the center of the sphere. Unless these forces are balanced in some way, the compressive dilatory forces will initiate cracks in the outer diamond layer and cause the construct to be unusable.

Typically, changes in bulk modulus of solid metal features in the construct are controlled by selecting metals with a compatible modulus of elasticity. The thickness and other sizing features are also important. CTE, on the other hand, is changed by the addition of diamond or other carbides to the gradient layers.

One embodiment, depicted in FIG. 21, involves the use of two gradient outer layers 2101 and 2102, a solid titanium layer 2103 and an inner CoCrMo sphere 2104. In this embodiment the first gradient layer provides a “sweep source” of biocompatible CoCrMo solvent metal to the outer diamond layer. The solid Titanium layer provides a dilatory source that offsets the CTE from the solid CoCrMo center ball and keeps it from “pulling away” from the Titanium/CoCrMo interface as the sintering pressure and temperature go from the 65 Kbar and 1400° C. sintering range to 1 bar and room temperature.

Where two or more powder based gradient layers are to be used in the construct it becomes increasingly important to control the CTE of each layer to ensure structural integrity following sintering. During the sintering process stresses are induced along the interface between each of the gradient layers. These high stresses are a direct result of the differences in the CTE between any two adjacent layers. To reduce these stresses one or both of the layer materials CTE's must be modified.

The CTE of the a substrate can be modified by either changing to a substrate with a CTE close to that of diamond (an example is the use of cemented Tungsten Carbide, where the CTE of Diamond is approximately 1.8 μm/m-° C. and Cemented Tungsten Carbide is Approximately 4.4 μm/m-° C.), or in the case of powdered layers, by adding a low CTE material to the substrate layer itself. That is, making a mixture of two or more materials, one or more of which will alter the CTE of the substrate layer.

Metal powders can be mixed with diamond or other superhard materials to produce a material with a CTE close to that of diamond and thus produce stresses low enough following sintering to prevent delamination of the layers at their interfaces. Experimental data shows that the CTE altering materials will not generally react with each other, which allows the investigator to predict the outcome of the intermediate CTE for each gradient level.

The desired CTE is obtained by mixing specific quantities of two materials according to the rule of mixtures. Table 10 shows the change in CTE between two materials, A and B as a function of composition (Volume Percent). In this example, materials A and B have CTE's of 150 and 600 μ In./In.−° F. respectively. By adding 50 mol % of A to 50 mol % of B the resulting CTE is 375 μ in/in−° F. One or more of the following component processes is incorporated into the mold release system:

-   -   1) An intermediate layer of material between the polycrystalline         diamond compact part and the mould that prevents bonding of the         polycrystalline diamond compact to the mould surface.     -   2) A mold material that does not bond to the polycrystalline         diamond compact under the conditions of synthesis.     -   3) A mold material that, in the final stages of, or at the         conclusion of, the polycrystalline diamond compact synthesis         cycle either contracts away from the polycrystalline diamond         compact in the case of a net concave polycrystalline diamond         compact geometry, or expands away from the polycrystalline         diamond compact in the case of a net convex polycrystalline         diamond compact geometry.     -   4) The mold shape can also act, simultaneously as a source of         sweep metal useful in the polycrystalline diamond compact         synthesis process.

As an example, a mold release system may be utilized in manufacturing a polycrystalline diamond compact by employing a negative shape of the desired geometry to produce heminon-planar parts. The mold surface contracts away from the final net concave geometry, the mold surface acts as a source of solvent-catalyst metal for the polycrystalline diamond compact synthesis process, and the mold surface has poor bonding properties to polycrystalline diamond compacts. TABLE 10 PREDICTED DIMENSIONAL CHANGES IN AN EIGHT INCH LAYERED CONSTRUCT CTE Total Length Final A % B % (μ In./In-° F.) Change (In.) Dimension (In.) 100 0 150 .0012 7.9988 90 10 195 .0016 7.9984 80 20 240 .0019 7.9981 70 30 285 .0023 7.9977 60 40 330 .0026 7.9974 50 50 375 .0030 7.9970 40 60 420 .0034 7.9966 30 70 465 .0037 7.9963 20 80 510 .0041 7.9959 10 90 555 .0044 7.9956 0 100 600 .0048 7.9952

Referring to FIG. 22, an illustration of how the above CTE modification works in a one-dimensional example. The one-dimensional example works as well in a three-dimensional construct. If the above materials A and B are packed in alternating layers 2201 and 2202 as shown in FIG. 22, separately in their pure forms, with their CTE's of 150 and 600 μ In./In.−° F. respectively, they will contract exactly 150 μ In./In.−° F. and 600 μ In./In.−° F. for every degree decrease in temperature. For an eight inch block of the one inch thick stacked layers the total change in dimension for a one degree decrease in temperature will be: Material A: (4×1 In.)×(0.00015 In./In.−° F.)×1° F.=0.006 In. Material B: (4×1 In.)×(0.00060 In./In.−° F.)×1)° F.=0.0024 In. Total overall length decrease in eight inches=0.0030 In.

By comparison, each of the layers is modified by using a mixture of 50% of A and 50% of B, and all eight layers are stacked into the eight-inch block configuration shown in FIG. 7. Re-calculation of the overall length decrease using the new composite CET of 375 μ In./In.−° F. from Table II shows: Material A+B: (8×1 In.)×(0.000375 In./In.−° F.)×1° F.=0.0030 In. Total overall length decrease in eight inches=0.0030 In.

The length decrease in this case was accurately predicted for the one-dimensional construct using one-inch thick layers by using the Rule of Mixtures.

Metals have very high CTE values as compared to diamond, which has one of the lowest CTE's of any known material. When metals are used as substrates for PDC and PCBN sintering considerable stress is developed at the interface. Therefore, mixing low CTE material with the biocompatible metal for medical implants can be used to reduce interfacial stresses. One of the best candidate materials is diamond itself. Other materials include refractory metal carbides and bitrides, and some oxides. Borides and silicides would also be good materials from a theoretical standpoint, but may not be biocompatible. The following is a list of candidate materials: Carbides Silicides Oxynitrides Nitrides Oxides Oxyborides Borides Oxycarbides Carbonitrides There are other materials and combinations of materials that could be utilized as CTE modifiers.

There are also other factors that also apply to the reduction of interface stresses for a particular geometrical construct. The thickness of the gradient layer, its position in the construct, and the general shape of the final construct all contribute in interfacial stress tensor reduction. Geometries that are more spherical tend to promote interface circumferential failures from positive or negative radial tensors while geometries of a cylindrical configuration tend to fail at the layer interfaces precipitated by bending stress couples.

The design of the gradient layers respecting CTE and the amount of contraction the each individual layer will experience during cooling form the HTHP sintering process will largely dictate the direction of stress tensors in the construct. Generally, the designer will always desire to have the outer wear layer of superhard material in compression to prevent delamination and crack propagation. In spherical geometries the stress tensors would be directed radially toward the center of the spherical shape giving special attention to the interfacial stresses at each layer interface to prevent failures at these interfaces as well. In cylindrical geometries the stress tensors would be adjusted to prevent stress couples from initiating cracks in either end of the cylinder, especially at the end where the wear surface is present.

The following are embodiments that relates to a spherical geometry wherein combinations of gradient layers and/or solid metal balls are used to control the final outcomes of the constructs. FIG. 23 is an embodiment that shows a spherical construct, which utilizes five gradient layers wherein the composition of each layer is described in Tables 11 and 12: TABLE 11 DIAMOND Cr3C2 CoCrMo LAYER Size Volume Volume Volume THICKNESS LAYER (μm) % % % (In.) First (Outer 20 92 8 0 .090 Layer) 2301 Second 2302 40 70 20 20 .104 Third 2303 70 60 20 20 .120 Forth 2304 70 60 26 26 .138 Fifth 2305 70 25 37.5 37.5 .154

TABLE 12 DIAMOND Cr3C2 CoCrMo LAYER Size Volume Volume Volume THICKNESS LAYER (μm) % % % (In.) First (Outer 20 100 0 0 .090 Layer) 2301 Second 2302 40 70 20 20 .104 Third 2304 70 60 20 20 .120 Forth 2304 70 60 26 26 .138 Fifth 2305 70 25 37.5 37.5 .154

FIG. 24 is an embodiment that shows a spherical construct, which utilizes four gradient layers wherein the composition of each layer is described in Tables 13 and 14. TABLE 13 DIAMOND Cr3C2 CoCrMo LAYER Size Volume Volume Volume THICKNESS LAYER (μm) % % % (In.) First (Outer 20 92 0 8 .097 Layer) 2401 Second 2402 40 70 10 20 .125 Third 2403 70 60 20 20 .144 Forth 2404 70 50 25 25 .240

TABLE 14 DIAMOND Cr3C2 CoCrMo LAYER Size Volume Volume Volume THICKNESS LAYER (μm) % % % (In.) First (Outer 20 100 0 0 .097 Layer) 2401 Second 2402 40 70 10 20 .125 Third 2403 70 60 20 20 .144 Forth 2404 70 50 25 25 .240

FIG. 25 shows an embodiment construct that utilizes a center support ball with gradient layers laid up on the ball and each other to form the complete construct. The inner ball of solid metal CoCrMo is encapsulate with a 0.003 to 0.010 inch thick refractory barrier can to prevent the over saturation of the system with the ball metal during the HTHP phase of sintering. The composition of each layer is described in Tables 15 and 16. TABLE 15 DIAMOND Cr3C2 CoCrMo LAYER Size Volume Volume Volume THICKNESS LAYER (μm) % % % (In.) First (Outer 20 92 0 8 .097 Layer) 2501 Second 2502 40 70 10 20 .125 Third 2503 70 60 20 20 .144 CoCrMo Ball N/A N/A N/A N/A N/A 2504

TABLE 16 DIAMOND Cr3C2 CoCrMo LAYER Size Volume Volume Volume THICKNESS LAYER (μm) % % % (In.) First (Outer 20 100 0 0 .097 Layer) 2501 Second 2502 40 70 10 20 .125 Third 2503 70 60 20 20 .144 CoCrMo Ball N/A N/A N/A N/A N/A 2504 Predicated on the end use function of the sphere above, the inner ball could be made of Cemented Tungsten Carbide, Niobium, Nickel, Stainless steel, Steel, or one of several other metal or ceramic materials to suite the designers needs.

Embodiments Relating to Dome Shapes are Described as Follow

FIG. 26 shows a dome embodiment construct that utilizes two gradient layers 2601 and 2602 wherein the composition of each layer is described in Tables 17 and 18. TABLE 17 DIAMOND Cr3C2 CoCrMo TiCTiN LAYER Size Volume Volume Volume Volume THICKNESS LAYER (μm) % % % % (In.) First (Outer 20 94 0 6 0.05 .200 Layer) 2602 Second 2601 70 60 20 20 0.05 .125

TABLE 18 DIAMOND Cr3C2 CoCrMo TiCTiN LAYER Size Volume Volume Volume Volume THICKNESS LAYER (μm) % % % % (In.) First (Outer 20 100 0 0 0.05 .200 Layer) 2602 Second 2601 70 60 20 20 0.05 .125

FIG. 27 shows a dome embodiment construct that utilizes two gradient layers 2701 and 2702 wherein the composition of each layer is described in Tables 19 and 20: TABLE 19 DIAMOND Cr3C2 CoCrMo TiCTiN LAYER Size Volume Volume Volume Volume THICKNESS LAYER (μm) % % % % (In.) First (Outer 20 94 0 6 0.05 .128 Layer) 2702 Second 2701 70 60 20 20 0.05 .230

TABLE 20 DIAMOND Cr3C2 CoCrMo TiCTiN LAYER Size Volume Volume Volume Volume THICKNESS LAYER (μm) % % % % (In.) First (Outer 20 100 0 0 0.05 .128 Layer) 2702 Second 2701 70 60 20 20 0.05 .230

FIG. 28 shows a dome embodiment construct that utilizes three gradient layers 2801, 2802 and 2803 where the composition of each layer is described in Tables 21 and 22: TABLE 21 DIAMOND Cr3C2 CoCrMo TiCTiN LAYER Size Volume Volume Volume Volume THICKNESS LAYER (μm) % % % % (In.) First (Outer 20 96 0 4 0.05 .168 Layer) 2801 Second 2802 40 80 10 10 0.05 .060 Third 2803 70 60 20 20 0.05 .130

TABLE 22 DIAMOND Cr3C2 CoCrMo TiCTiN LAYER Size Volume Volume Volume Volume THICKNESS LAYER (μm) % % % % (In.) First (Outer 20 100 0 0 0.05 .168 Layer) 2801 Second 2802 40 80 10 10 0.05 .060 Third 2803 70 60 20 20 0.05 .130

FIG. 29 shows a dome embodiment construct that utilizes three gradient layers 2901, 2902 and 9803 wherein the composition of each layer is described in Tables 23 and 24: TABLE 23 DIAMOND Cr3C2 CoCrMo TiCTiN LAYER Size Volume Volume Volume Volume THICKNESS LAYER (μm) % % % % (In.) First (Outer 20 96 0 4 0.05 .065 Layer) 2901 Second 2902 40 80 10 10 0.05 .050 Third 2903 70 60 20 20 0.05 .243

TABLE 24 DIAMOND Cr3C2 CoCrMo TiCTiN LAYER Size Volume Volume Volume Volume THICKNESS LAYER (μm) % % % % (In.) First (Outer 20 100 0 0 0.05 .065 Layer) 2901 Second 2902 40 80 10 10 0.05 .050 Third 2903 70 60 20 20 0.05 .243

Embodiments Relating to Flat Cylindrical Shapes are Described as Follows

FIG. 30 shows a flat cylindrical embodiment construct that utilizes two gradient layers 3001 and 3002 wherein the composition of each layer is described in Tables 25 and 26: TABLE 25 DIAMOND Cr3C2 CoCrMo TiCTiN LAYER Size Volume Volume Volume Volume THICKNESS LAYER (μm) % % % % (In.) First (Outer 20 94 0 6 0.05 Layer) 3001 Second 3002 70 60 20 20 0.05

TABLE 26 DIAMOND Cr3C2 CoCrMo TiCTiN LAYER Size Volume Volume Volume Volume THICKNESS LAYER (μm) % % % % (In.) First (Outer 20 100 0 0 0.05 Layer) 3001 Second 3002 70 60 20 20 0.05

FIG. 31 shows a flat cylindrical embodiment construct that utilizes three gradient layers 3101, 3102, 3103 wherein the composition of each layer is described in Tables 27 and 28: TABLE 27 DIAMOND Cr3C2 CoCrMo TiCTiN LAYER Size Volume Volume Volume Volume THICKNESS LAYER (μm) % % % % (In.) First (Outer 20 96 0 4 0.05 Layer) 3101 Second 3102 40 80 10 10 0.05 Third 3103 70 60 20 20 0.05

TABLE 28 DIAMOND Cr3C2 CoCrMo TiCTiN LAYER Size Volume Volume Volume Volume THICKNESS LAYER (μm) % % % % (In.) First (Outer 20 100 0 0 0.05 Layer) 3101 Second 3102 40 80 10 10 0.05 Third 3103 70 60 20 20 0.05

FIG. 32 shows a flat cylindrical embodiment construct that utilizes three gradient layers 3201, 3202, 3203 laid up on a CoCrMo substrate 3204. The cylindrical substrate of solid metal CoCrMo is encapsulate with a 0.003 to 0.010 inch thick refractory barrier can 3205 to prevent the over saturation of the system with the substrate metal during the HTHP phase of sintering. The composition of each layer is described in Tables 29 and 30: TABLE 29 DIAMOND Cr3C2 CoCrMo TiCTiN LAYER Size Volume Volume Volume Volume THICKNESS LAYER (μm) % % % % (In.) First (Outer 20 96 0 4 0.05 Layer) 3201 Second 3202 40 80 10 10 0.05 Third 3203 70 60 20 20 0.05 CoCrMo Substrate N/A N/A N/A N/A N/A 3204

TABLE 30 DIAMOND Cr3C2 CoCrMo TiCTiN LAYER Size Volume Volume Volume Volume THICKNESS LAYER (μm) % % % % (In.) First (Outer 20 100 0 0 0.05 Layer) 3201 Second 3202 40 80 10 10 0.05 Third 3203 70 60 20 20 0.05 CoCrMo Substrate N/A N/A N/A N/A N/A 3204

Predicated on the end use function of the cylinder shape of FIG. 32 the inner substrate could be made of Cemented Tungsten Carbide, Niobium, Nickel, Stainless steel, Steel, or one of several other metal or ceramic materials to suite the designers needs.

Embodiments Relating to Flat Cylindrical Shapes with Formed-in-Place Concave Features are Described as Follow

FIG. 33 show an embodiment of a flat cylindrical shape with a formed in place concave trough 3303 that utilizes two gradient layers 3301 and 3302 wherein the composition of each layer is described in Tables 31 and 32: TABLE 31 LAYER DIAMOND Cr3C2 CoCrMo TiCTiN THICKNESS LAYER Size (μm) Volume % Volume % Volume % Volume % (In.) First (Outer Layer) 20 94 0 6 0.05 .156 3301 Second 3302 70 60 20 20 0.05 .060 Filler Support 3303 70 60 20 20 0.05 N/A

TABLE 32 LAYER DIAMOND Cr3C2 CoCrMo TiCTiN THICKNESS LAYER Size (μm) Volume % Volume % Volume % Volume % (In.) First (Outer Layer) 20 100 0 0 0.05 .156 3301 Second 3302 70 60 20 20 0.05 .060 Filler Support 3303 70 60 20 20 0.05 N/A

FIG. 34 shows an embodiment of a flat cylindrical shape with a formed in place concave trough 3402 that utilizes two gradient layers 3401 and 3402 wherein the composition of each layer is described in Tables 33 and 34: TABLE 33 LAYER DIAMOND Cr3C2 CoCrMo TiCTiN THICKNESS LAYER Size (μm) Volume % Volume % Volume % Volume % (In.) First (Outer Layer) 20 94 0 6 0.05 .156 3401 Second 3402 70 60 20 20 0.05 .060 Filler Support 3403 70 60 20 20 0.05 N/A

TABLE 34 LAYER DIAMOND Cr3C2 CoCrMo TiCTiN THICKNESS LAYER Size (μm) Volume % Volume % Volume % Volume % (In.) First (Outer Layer) 20 100 0 0 0.05 .156 3401 Second 3402 70 60 20 20 0.05 .060 Filler Support 3403 70 60 20 20 0.05 N/A

FIG. 35 shows an embodiment of a flat cylindrical shape with a formed in place concave 3504 trough that utilizes three gradient layers 3501, 3502, 2503 wherein the composition of each layer is described in Tables 35 and 36: TABLE 35 LAYER DIAMOND Cr3C2 CoCrMo TiCTiN THICKNESS LAYER Size (μm) Volume % Volume % Volume % Volume % (In.) First (Outer Layer) 20 96 0 4 0.05 .110 3501 Second 3502 40 80 10 10 0.05 .040 Third 2503 70 60 20 20 0.05 .057 Filler Support 3504 70 60 20 20 0.05 N/A

TABLE 36 LAYER DIAMOND Cr3C2 CoCrMo TiCTiN THICKNESS LAYER Size (μm) Volume % Volume % Volume % Volume % (In.) First (Outer Layer) 20 100 0 0 0.05 .110 3501 Second 3502 40 80 10 10 0.05 .040 Third 3503 70 60 20 20 0.05 .057 Filler Support 3504 70 60 20 20 0.05 N/A

FIG. 36 shows an embodiment of a flat cylindrical shape with a formed in place concave trough 3604 that utilizes three gradient layers 3601, 3602, 3603 wherein the composition of each layer is described in Tables 37 and 38: TABLE 37 LAYER DIAMOND Cr3C2 CoCrMo TiCTiN THICKNESS LAYER Size (μm) Volume % Volume % Volume % Volume % (In.) First (Outer Layer) 20 96 0 4 0.05 .110 3601 Second 3602 40 80 10 10 0.05 .040 Third 3603 70 60 20 20 0.05 .057 Filler Support 3604 70 60 20 20 0.05 N/A

TABLE 38 LAYER DIAMOND Cr3C2 CoCrMo TiCTiN THICKNESS LAYER Size (μm) Volume % Volume % Volume % Volume % (In.) First (Outer Layer) 20 100 0 0 0.05 .110 3601 Second 3602 40 80 10 10 0.05 .040 Third 3603 70 60 20 20 0.05 .057 Filler Support 3604 70 60 20 20 0.05 N/A

Prepare Heater Assembly

In order to sinter the assembled and loaded diamond feedstock described above into polycrystalline diamond, both heat and pressure are required. Heat is provided electrically as the part undergoes pressure in a press. A heater assembly is used to provide the required heat.

A refractory metal can containing loaded and precompressed diamond feedstock is placed into a heater assembly. Salt domes are used to encase the can. The salt domes used may be white salt (NaCl) that is precompressed to at least about 90-95% of theoretical density. This density of the salt is desired to preserve high pressures of the sintering system and to maintain geometrical stability of the manufactured part. The salt domes and can are placed into a graphite heater tube assembly. The salt and graphite components of the heater assembly may be baked in a vacuum oven at greater than 100 degrees Celsius and at a vacuum of at least 23 torr for about 1 hour in order to eliminate adsorped water prior to loading in the heater assembly. Other materials which may be used in construction of a heater assembly include solid or foil graphite, amorphous carbon, pyrolitic carbon, refractory metals and high electrical resistant metals.

Once electrical power is supplied to the heater tube, it will generate heat required for polycrystalline diamond formation in the high pressure/high temperature pressing operation.

Preparation of Pressure Assembly for Sintering

Once a heater assembly has been prepared, it is placed into a pressure assembly for sintering in a press under high pressure and high temperature. A cubic press or a belt press may be used for this purpose, with the pressure assembly differing somewhat depending on the type of press used. The pressure assembly is intended to receive pressure from a press and transfer it to the diamond feedstock so that sintering of the diamond may occur under isostatic conditions.

If a cubic press is used, then a cube of suitable pressure transfer media such as pyrophillite will contain the heater assembly. Cell pressure medium would be used if sintering were to take place in a belt press. Salt may be used as a pressure transfer media between the cube and the heater assembly. Thermocouples may be used on the cube to monitor temperature during sintering. The cube with the heater assembly inside of it is considered a pressure assembly, and is place into a press a press for sintering.

Sintering of Feedstock into Polycrystalline Diamond

The pressure assembly described above containing a refractory metal can that has diamond feedstock loaded and precompressed within is placed into an appropriate press. The type of press used at the time of the devices may be a cubic press (i.e., the press has six anvil faces) for transmitting high pressure to the assembly along 3 axes from six different directions. Alternatively, a belt press and a cylindrical cell can be used to obtain similar results. Other presses may be used as well. Referring to FIG. 37, a representation of the 6 anvils of a cubic press 3720 is provided. The anvils 3721, 3722, 3723, 3724, 3725 and 3726 are situated around a pressure assembly 3730.

To prepare for sintering, the entire pressure assembly is loaded into a press and initially pressurized to about 40-68 Kbars. The pressure to be used depends on the product to be manufactured and must be determined empirically. Then electrical power may be added to the pressure assembly in order to reach a temperature in the range of less than about 1145 or 1200 to more than about 1500 degrees Celsius. About 5800 watts of electrical power may be used at two opposing anvil faces, creating the current flow required for the heater assembly to generate the desired level of heat. Once the desired temperature is reached, the pressure assembly is subjected to pressure of about 1 million pounds per square inch at the anvil face. The components of the pressure assembly transmit pressure to the diamond feedstock. These conditions may be maintained for about 3-12 minutes, but could be from less than 1 minute to more than 30 minutes. The sintering of polycrystalline diamond compacts takes place in an isostatic environment where the pressure transfer components are permitted only to change in volume but are not permitted to otherwise deform. Once the sintering cycle is complete, about a 90 second cool down period is allowed, and then pressure is removed. The polycrystalline diamond compact is then removed for finishing.

Removal of a sintered polycrystalline diamond compact having a curved, compound or complex shape from a pressure assembly is simple due to the differences in material properties between diamond and the surrounding metals in some embodiments of the devices. This is generally referred to as the mold release system of the devices.

Removal of Solvent-Catalyst Metal from PCD

If desired, the solvent-catalyst metal remaining in interstitial spaces of the sintered polycrystalline diamond may be removed. Such removal is accomplished by chemical leaching as is known in the art. After solvent-catalyst metal has been removed from the interstitial spaces in the diamond table, the diamond table will have greater stability at high temperatures. This is because there is no catalyst for the diamond to react with and break down.

After leaching solvent-catalyst metal from the diamond table, it may be replaced by another metal, metal or metal compound in order to form thermally stable diamond that is stronger than leached polycrystalline diamond. If it is intended to weld synthetic diamond or a polycrystalline diamond compact to a substrate or to another surface such as by inertia welding, it may be desirable to use thermally stable diamond due to its resistance to heat generated by the welding process.

Finishing Methods and Apparatuses

Once a polycrystalline diamond compact has been sintered, a mechanical finishing process may be employed to prepare the final product. The finishing steps explained below are described with respect to finishing a polycrystalline diamond compact, but they could be used to finish any other surface or any other type of component.

Prior to the devices herein, the synthetic diamond industry was faced with the problem of finishing flat surfaces and thin edges of diamond compacts. Methods for removal of large amounts of diamond from non-planar surfaces or finishing those surfaces to high degrees of accuracy for sphericity, size and surface finish had not been developed in the past.

Finishing of Superhard Cylindrical and Flat Forms.

In order to provide a greater perspective on finishing techniques for curved and non-planar superhard surfaces for nozzles, a description of other finishing techniques is provided.

Lapping.

A wet slurry of diamond grit on cast iron or copper rotating plates are used to remove material on larger flat surfaces (e.g., up to about 70 mm. in diameter). End coated cylinders of size ranging from about 3 mm to about 70 mm may also be lapped to create flat surfaces. Lapping is generally slow and not dimensionally controllable for depth and layer thickness, although flatness and surface finishes can be held to very close tolerances.

Grinding.

Diamond impregnated grinding wheels are used to shape cylindrical and flat surfaces. Grinding wheels are usually resin bonded in a variety of different shapes depending on the type of material removal required (i.e., cylindrical centerless grinding or edge grinding). Polycrystalline diamond compacts are difficult to grind, and large polycrystalline diamond compact surfaces are nearly impossible to grind. Consequently, it is desirable to keep grinding to a minimum, and grinding is usually confined to a narrow edge or perimeter or to the sharpening of a sized PDC end-coated cylinder or machine tool insert.

Electro Spark Discharge Grinding (EDG).

Rough machining of polycrystalline diamond compact may be accomplished with electro spark discharge grinding (“EDG”) on large diameter (e.g., up to about 70 mm.) flat surfaces. This technology typically involves the use of a rotating carbon wheel with a positive electrical current running against a polycrystalline diamond compact flat surface with a negative electrical potential. The automatic controls of the EDG machine maintain proper electrical erosion of the polycrystalline diamond compact material by controlling variables such as spark frequency, voltage and others. EDG is typically a more efficient method for removing larger volumes of diamond than lapping or grinding. After EDG, the surface must be finish lapped or ground to remove what is referred to as the heat affected area or re-cast layer left by EDG.

Wire Electrical Discharge Machining (WEDM).

WEDM is used to cut superhard parts of various shapes and sizes from larger cylinders or flat pieces. Typically, cutting tips and inserts for machine tools and re-shaping cutters for oil well drilling bits represent the greatest use for WEDM in PDC finishing.

Polishing.

Polishing superhard surfaces for nozzles to very high tolerances may be accomplished by diamond impregnated high speed polishing machines. The combination of high speed and high friction temperatures tends to burnish a PDC surface finished by this method, while maintaining high degrees of flatness, thereby producing a mirror-like appearance with precise dimensional accuracy.

b. Finishing a Non-Planar Geometry.

Finishing a non-planar surface (concave non-planar or convex non-planar) presents a greater problem than finishing a flat surface or the rounded edge of a cylinder. The total surface area of a sphere to be finished compared to the total surface area of a round end of a cylinder of like radius is four (4) times greater, resulting in the need to remove four (4) times the amount of polycrystalline diamond compact material. The nature of a non-planar surface makes traditional processing techniques such as lapping, grinding and others unusable because they are adapted to flat and cylindrical surfaces. The contact point on a sphere should be point contact that is tangential to the edge of the sphere, resulting in a smaller amount of material removed per unit of time, and a proportional increase in finishing time required. Also, the design and types of processing equipment and tooling required for finishing non-planar objects must be more accurate and must function to closer tolerances than those for other shapes. Non-planar finishing equipment also requires greater degrees of adjustment for positioning the workpiece and tool ingress and egress.

The following are steps that may be performed in order to finish a non-planar, rounded or arcuate surface.

1.) Rough Machining.

Initially roughing out the dimensions of the surface using a specialized electrical discharge machining apparatus may be performed. Referring to FIG. 38, roughing a polycrystalline diamond compact sphere 3803 is depicted. A rotator 3802 is provided that is continuously rotatable about its longitudinal axis (the z axis depicted). The sphere 3803 to be roughed is attached to a spindle of the rotator 3802. An electrode 3801 is provided with a contact end 3801A that is shaped to accommodate the part to be roughed. In this case the contact end 3801A has a partially non-planar shape. The electrode 3801 is rotated continuously about its longitudinal axis (the y axis depicted). Angular orientation of the longitudinal axis y of the electrode 3801 with respect to the longitudinal axis z of the rotator 3802 at a desired angle β is adjusted to cause the electrode 3801 to remove material from the entire non-planar surface of the ball 3803 as desired.

Thus, the electrode 3801 and the sphere 3803 are rotating about different axes. Adjustment of the axes can be used to achieve near perfect non-planar movement of the part to be roughed. Consequently, a nearly perfect non-planar part results from this process. This method produces polycrystalline diamond compact non-planar surfaces with a high degree of sphericity and cut to very close tolerances. By controlling the amount of current introduced to the erosion prQcess, the depth and amount of the heat affected zone can be minimized. In the case of a polycrystalline diamond compact, the heat affected zone can be kept to about 3 to 5 microns in depth and is easily removed by grinding and polishing with diamond impregnated grinding and polishing wheels.

Referring to FIG. 39, roughing a convex non-planar polycrystalline diamond compact 1003 such as a nozzle is depicted. A rotator 3902 is provided that is continuously rotatable about its longitudinal axis (the z axis depicted). The part 3903 to be roughed is attached to a spindle of the rotator 3902. An electrode 3901 is provided with a contact end 3901A that is shaped to accommodate the part to be roughed. The electrode 3901 is continuously rotatable about its longitudinal axis (the y axis depicted). Angular orientation of the longitudinal axis y of the electrode 3901 with respect to the longitudinal axis z of the rotator 3902 at a desired angle β is adjusted to cause the electrode 3901 to remove material from the entire non-planar surface of the nozzle 3903 as desired.

In some embodiments of the devices, multiple electro discharge machine electrodes will be used in succession in order to machine a part. A battery of electro discharge machines may be employed to carry this out in assembly line fashion. Further refinements to machining processes and apparatuses are described below.

Complex positive or negative relief (concave or convex) forms can be machined into Polycrystalline Diamond Compacts (PDC) or Polycrystalline cubic Boron Nitride (PCBN) parts. This a standard Electrical Discharge Machining (EDM) CNC machining center and suitably machined electrodes accomplish the desired forms.

FIG. 40 (side view) and FIG. 40 a (end view) show an electrode 4001 with a convex form 4002 machined on the active end of the electrode 4001, and the electrode base 4005. FIG. 41 (cross section at 41-41) and FIG. 41 a show an electrode 4101 with a concave form 4102 and base 4105. The opposite ends of the electrodes are provided with an attachment mechanism at the base 4105 suitable for the particular EDM machine being utilized. There are a variety of electrode materials that can be utilized such a copper, copper tungsten, graphite, and combinations of graphite and metal mixes. Materials best suited for machining PDC and PCBN are copper tungsten for roughing and pure graphite, or graphite copper tungsten mixes. Not all EDM machines are capable of machining PDC and PCBN. Only those equipped with capacitor discharge power supplies can generate spark intensities with enough power to efficiently erode these materials.

The actual size of the machined relief form is usually machined undersized to allow for a suitable spark gap for the burning/erosion process to take place. Each spark gap length dictates a set of machining parameters that must be set by the machine operator to ensure efficient electrical discharge erosion of the material to be removed. Normally, two to four electrodes are prepared with different spark gap allowances. For example, an electrode using a 0.006 In. spark gap could be prepared for “roughing,” and an “interim” electrode at 0.002 In. spark gap, and “finishing” electrode at 0.0005 In. spark gap. In each case the machining voltage (V), peak amperage (AP), pulse duration (P), reference frequency (RF), pulse duration (A), retract duration (R), under-the-cut duration (U), and servo voltage (SV) must be set up within the machines control system.

FIG. 42 shows an EDM relief form 4201 sinking operation in a PDC insert part 4202. Table 39 describes the settings for the using a copper tungsten electrode 4203 for roughing and a graphite/copper tungsten electrode for finishing. The spark gap 4204 is also depicted. TABLE 39 Spark Electrode Gap 4203 4204 V AP P RF A R U SV Roughing .006 −2 7 13 56 9 0 9 50 Finishing .001 −5 4 2 60 2 0 9 55

Those familiar with the field of EDM machining will recognize that variations in the parameters show will be required based on the electrode configuration, electrode wear rates desired, and surface finishes required. Generally, higher machining rates, i.e., higher values of “V” and “AP” produce higher rates of discharge erosion, but conversely rougher surface finishes.

Obtaining very smooth and accurate finishes also requires the use of a proper dielectric machining fluid. Synthetic hydrocarbons with satellite electrodes as disclosed in U.S. Pat. No. 5,773,782, which is hereby incorporated by reference, appear to assist in obtaining high quality surface finishes.

FIG. 43 shows an embodiment wherein a single ball-nosed (spherical radiused) EDM electrode 4301 is used to form a concave relief form 4303 in a PDC or PCBN part 4302. The electrode 4301 is plunged vertically into the part 4302 and then moved laterally to accomplish the rest of the desired shape. By programming a CNC system EDM electrode “cutting path” of the EDM machine, an infinite variety of concave or convex shapes can be machined. Controlling the rate of “down” plunging and “lateral” cross cutting, and using the correct EDM material will dictate the quality of the size dimensions and surface finishes obtained.

2.) Finish Grinding and Polishing.

Once the non-planar surface (whether concave or convex) has been rough machined as described above or by other methods, finish grinding and polishing of a part can take place. Grinding is intended to remove the heat affected zone in the polycrystalline diamond compact material left behind by electrodes.

In some embodiments of the devices, grinding utilizes a grit size ranging from 100 to 150 according to standard ANSI B74.16-1971 and polishing utilizes a grit size ranging from 240 to 1500, although grit size may be selected according to the user's preference. Wheel speed for grinding should be adjusted by the user to achieve a favorable material removal rate, depending on grit size and the material being ground. A small amount of experimentation can be used to determine appropriate wheel speed for grinding. Once the spherical surface (whether concave or convex) has been rough machined as described above or by other methods, finish grinding and polishing of a part can take place. Grinding is intended to remove the heat affected zone in the polycrystalline diamond compact material left behind by electrodes. Use of the same rotational geometry as depicted in FIGS. 9 and 10 allows sphericity of the part to be maintained while improving its surface finish characteristics.

Referring to FIG. 44, it can be seen that a rotator 4401 holds a part to be finished 4403, in this case a convex sphere, by use of a spindle. The rotator 4401 is rotated continuously about its longitudinal axis (the z axis). A grinding or polishing wheel 4402 is provided is rotated continuously about its longitudinal axis (the x axis). The moving part 4403 is contacted with the moving grinding or polishing wheel 4402. The angular orientation β of the rotator 4401 with respect to the grinding or polishing wheel 4402 may be adjusted and oscillated to effect grinding or polishing of the part (ball or socket) across its entire surface and to maintain sphericity.

Referring to FIG. 45, it can be seen that a rotator 4501 holds a part to be finished 4503, in this case a convex spherical cup or race, by use of a spindle. The rotator 4501 is rotated continuously about its longitudinal axis (the z axis). A grinding or polishing wheel 4502 is provided that is continuously rotatable about its longitudinal axis (the x axis). The moving part 4503 is contacted with the moving grinding or polishing wheel 4502. The angular orientation β of the rotator 4501 with respect to the grinding or polishing wheel 4502 may be adjusted and oscillated if required to effect grinding or polishing of the part across the spherical portion of it surface.

In one embodiment, grinding utilizes a grit size ranging from 100 to 150 according to standard ANSI B74.16-1971 and polishing utilizes a grit size ranging from 240 to 1500, although grit size may be selected according to the user's preference. Wheel speed for grinding should be adjusted by the user to achieve a favorable material removal rate, depending on grit size and the material being ground. A small amount of experimentation can be used to determine appropriate wheel speed for grinding.

As desired, a diamond abrasive hollow grill may be used for polishing diamond or superhard bearing surfaces. A diamond abrasive hollow grill includes a hollow tube with a diamond matrix of metal, ceramic and resin (polymer) is found.

If a diamond surface is being polished, then the wheel speed for polishing mayl be adjusted to cause a temperature increase or heat buildup on the diamond surface. This heat buildup will cause burnishing of the diamond crystals to create a very smooth and mirror-like low friction surface. Actual material removal during polishing of diamond is not as important as removal sub-micron sized asperities in the surface by a high temperature burnishing action of diamond particles rubbing against each other. A surface speed of 6000 feet per minute minimum is generally required together with a high degree of pressure to carry out burnishing. Surface speeds of 4000 to 10,000 feet per minute are believed to be the most desirable range. Depending on pressure applied to the diamond being polished, polishing may be carried out at from about 500 linear feet per minute and 20,000 linear feet per minute.

Pressure must be applied to the workpiece in order to raise the temperature of the part being polished and thus to achieve the most desired mirror-like polish, but temperature should not be increased to the point that it causes complete degradation of the resin bond that holds the diamond polishing wheel matrix together, or resin will be deposited on the diamond. Excessive heat will also unnecessarily degrade the surface of the diamond.

Maintaining a constant flow of coolant (such as water) across the diamond surface being polished, maintaining an appropriate wheel speed such as 6000 linear feet per minute, applying sufficient pressure against the diamond to cause heat buildup but not so much as to degrade the wheel or damage the diamond, and timing the polishing appropriately are all important and must all be determined and adjusted according to the particular equipment being used and the particular part being polished. Generally the surface temperature of the diamond being polished should not be permitted to rise above 800 degrees Celsius or excessive degradation of the diamond will occur. Desirable surface finishing of the diamond, called burnishing, generally occurs between 650 and 750 degrees Celsius.

During polishing it is important to achieve a surface finish that has the lowest possible coefficient of friction, thereby providing a low friction and long-lasting articulation surface. Preferably, once a diamond or other superhard surface is formed in a bearing component, the surface is then polished to an Ra value of 0.3 to 0.005 microns. Acceptable polishing will include an Ra value in the range of 0.5 to 0.005 microns or less. The parts of the bearing component may be polished individually before assembly or as a unit after assembly. Other methods of polishing polycrystalline diamond compacts and other superhard materials could be adapted to work with the articulation surfaces of the invented bearing components, with the objective being to achieve a smooth surface, preferably with an Ra value of 0.01-0.005 microns. Further grinding and polishing details are provided below.

FIG. 46 shows a diamond grinding form 4601 mounted to an arbor 4602, which is in turn mounted into the high-speed spindle 4603 of a CNC grinding machine. The cutting path motion 4604 of the grinding form 4601 is controlled by the CNC program allowing the necessary surface coverage requiring grinding or polishing. The spindle speed is generally related to the diameter of the grinding form and the surface speed desired at the interface with the material 4505 to be removed. The surface speed should range between 4,000 and 17,000 feet per minuet for both grinding and polishing. For grinding, the basic grinding media for the grinding form should be as “free” cutting as practical with diamond grit sizes in the range of 80 to 120 microns and concentrations ranging from 75 to 125. For polishing the grinding media should not be as “free cutting,” i.e., the grinding form should generally be harder and denser with grit sizes ranging from 120 to 300 microns and concentrations ranging from 100 to 150.

Superhard materials can be more readily removed by grinding if the actual area of the material being removed is kept as small as possible. Ideally the bruiting form 4601 should be rotated to create conditions in the range from 20,000 to 40,000 surface feet per minuet between the part 4605 and the bruiting form 4601. Spindle pressure between the part 4605 and the bruiting form 4601 operating in a range of 10 to 100 Lbs—force producing an interface temperature between 650 and 750 Deg C. is required. Cooling water is needed to take away excess heat to keep the part from failing possible. The simplest way to keep the grind area small is to utilize a small cylindrical contact point (usually a ball form, although a radiused end of a cylinder accomplishes the same purpose), operating against a larger surface area.

FIGS. 47 shows the tangential area of contact 4620 between the grinding form 4601 and the substantially larger superhard material 4621. By controlling the path of the grinding form cutter, small grooves 4630 (FIG. 48) can be ground into the surface of the superhard material 4621 removing the material and leaving small “cusp” 4640 between the adjacent grooves. As the grooves are cut shallower and closer together the “cusp” 4640 become imperceptible to the naked eye and are easily removed by subsequent polishing operations. The cutter line path of the grinding form cutter should be controlled by programming the CNC system of the grinding machine to optimize the cusp size, grinding form cutter wear, and material removal rates.

Bruting

Obtaining highly polished surface finishes on Polycrystalline Diamond Compact (PDC), Polycrystalline Cubic Boron Nitride (PBCN), and other superhard materials in the range of 0.05 to 0.005 μm can be obtained by running PDC form against the surface to be polished. “Bruiting” or rubbing a diamond surface under high pressure and temperature against another superhard material degredates or burns away any positive asperities remaining from previous grinding and polishing operations producing a surface finish not obtainable in any other way.

FIG. 49 shows a PDC dome part 4901 on a holder 4904 and being “Bruit Polished” using a PDC bruiting form 4902 being rotated in a high-speed spindle 4903. Ideally the bruiting form should be rotated in a range from 20,000 to 40,000 surface feet per minute with the spindle pressure operating in a range of 10 to 100 Lbs—force producing an interface temperature between 650 and 750 Deg C. Cooling water is generally required to take away excess heat to keep the part from failing.

FIG. 50 shows another embodiment of the bruiting polishing technique wherein the PDC Bruiting form 5001 is controlled through a complex surface path 5002 by a CNC system of a grinding machine or a CNC Mill equipped with a high-speed spindle to control the point of contact 5003 of the form 5001 with a superhard component 5004.

FIGS. 51 a-114 b depict various nozzles or nozzle components which utilize superhard constrictions, flow surfaces, diverters, grooves, orifice rims, plugs, tips, distributors, cores, liners, inserts, and other parts for any type of material flow, including wet or dry particles, liquids or gases, abrasive or non-abrasive materials, and corrosive or caustic materials well as non-corrosive and non-caustic materials. In each of these applications and others, the superhard materials, such as sintered polycrystalline diamond compacts and others mentioned herein, provide a low-wear highly durable surface for use in a nozzle. A diamond table bonded to a substrate may be used in some embodiments, and in other embodiments free standing diamond may be used.

Referring to FIGS. 51 a and 51 b, a cross sectional view and an end view, respectively, are provided of a nozzle or nozzle component 5101 having a body 5102 and an orifice 5103. The body 5102 includes a sintered polycrystalline diamond compact that has a diamond table 5104 on a substrate 5105. The example orifice 5103 depicted may be divergent, straight, conical, reverse conical, radiused or otherwise. The orifice may include a sharp or radiused edge. The shading of the diamond table 5104 and the substrate 5105 used for this figure are consistent throughout the remaining figures to permit the reader to readily distinguish the diamond table from the substrate and other components.

Referring to FIGS. 52 a and 52 b, a cross sectional view and an end view, respectively, are provided of a nozzle or nozzle component 5201 having a body 5202 and an orifice 5203. The body 5202 includes a sintered polycrystalline diamond compact that has a free standing diamond table 5204. The example orifice 5103 depicted may be divergent, straight, conical, reverse conical, radiused or otherwise. The orifice may include a sharp or radiused edge.

Referring to FIGS. 53 a and 53 b, a cross sectional view and an end view, respectively, are provided of a nozzle or nozzle component 5301. The orifice or aperture may have a divergent straight or radiused conic outlet and an extended cylindrical bore surface.

Referring to FIGS. 54 a and 54 b, a cross sectional view and an end view, respectively, are provided of a nozzle or nozzle component 5401. The orifice or aperture may be a convergent, straight, radiused or conic outlet and may include an extended cylindrical bore surface.

Referring to FIGS. 55 a and 55 b, a cross sectional view and an end view, respectively, are provided of a nozzle or nozzle component 5501. The orifice or aperture may be a straight through cylindrical bore.

Referring to FIGS. 56 a and 56 b, a cross sectional view and an end view, respectively, are provided of a nozzle or nozzle component 5601. The dual orifices may be straight through cylindrical bores.

Referring to FIGS. 57 a and 57 b, a cross sectional view and an end view, respectively, are provided of a nozzle or nozzle component 5701. The quad orifices may be angled or divergent straight through cylindrical bores.

Referring to FIGS. 58 a and 58 b, a cross sectional view and an end view, respectively, are provided of a nozzle or nozzle component 5801. The orifice may be a venturi type orifice that has a cross section defined by a hyperbola or twin opposing arcs. An auxiliary liquid, gas or particle introducing passage 5802 is provided.

Referring to FIGS. 59 a and 59 b, a cross sectional view and an end view, respectively, are provided of a nozzle or nozzle component 5901. The component depicted is a sintered polycrystalline diamond compact formed as a hemispherical cup.

Referring to FIGS. 60 a and 60 b, a cross sectional view and an end view, respectively, are provided of a nozzle or nozzle component 6001. The component depicted is a sintered polycrystalline diamond compact formed from free standing diamond as a hemispherical cup. The quad non-parallel orifices are shown spaced around the surface of the cup.

Referring to FIGS. 61 a and 61 b, a cross sectional view and an end view, respectively, are provided of a nozzle or nozzle component 6101. The orifice may be straight, radial inward or conical with a sharp edge.

Referring to FIGS. 62 a and 62 b, a cross sectional view and an end view, respectively, are provided of a nozzle or nozzle component 6201. The orifice may be straight, radial outward or conical with a sharp edge.

Referring to FIGS. 63 a and 63 b, a cross sectional view and an end view, respectively, are provided of a nozzle or nozzle component 6301. The orifice may have a straight cylindrical bore followed by a conical outward section.

Referring to FIGS. 64 a and 64 b, a cross sectional view and an end view, respectively, are provided of a nozzle or nozzle component 6401. The orifice may have an inward conical section followed by a straight cylindrical bore.

Referring to FIGS. 65 a and 65 b, a cross sectional view and an end view, respectively, are provided of a nozzle or nozzle component 6501. The nozzle includes a substrate and a diamond table. In the vicinity of the orifice, there is an outwardly protruding nipple 6502. The orifice is a straight cylindrical bore through the substrate and the diamond table.

Referring to FIGS. 66 a and 66 b, a cross sectional view and an end view, respectively, are provided of a nozzle or nozzle component 6601. The orifice may be a small hole followed on the outside of the nozzle by an oval or elliptical relief.

Referring to FIGS. 67 a, 67 b and 63 c, a cross sectional view, a side view and an end view, respectively, are provided of a nozzle or nozzle component 6701. The nozzle may have a straight cylindrical bore within it with a small side port orifice about which is cut a trough or V-groove. Such a nozzle may be formed by using a CoCr mold where the bore should be. Following sintering the CoCr will shrink away from the diamond table, leaving a hollow bore. The orifice and groove may be ground, machined or cut.

Referring to FIGS. 68 a, 68 b and 68 c, a cross sectional view, a side view and an end view, respectively, are provided of a nozzle or nozzle component 6801. The nozzle may have a straight cylindrical bore within it with a small side port orifice about which is cut a trough or U-groove.

Referring to FIGS. 69 a, 69 b and 69 c, a cross sectional view, a side view and an end view, respectively, are provided of a nozzle or nozzle component 6901. The nozzle may have a straight cylindrical bore 6902 within it with a small side port entry orifice 6903 for inflow of material and an exit orifice 6904 such as a V-cut for output of material. The bore 6902 may be plugged 6905.

Referring to FIGS. 70 a, 70 b and 70 c, a cross sectional view, a side view and an end view, respectively, are provided of a nozzle or nozzle component 7001. The nozzle may have a straight cylindrical bore within it with a small side port entry orifice for inflow of material and an exit orifice such as a U-trough for output of material. The bore may be plugged at its ends.

Referring to FIGS. 71 a and 71 b, a cross sectional view and an end view, respectively, are provided of a nozzle or nozzle component 7101. The nozzle has a hemispherical end section 7102, a cylindrical shank portion 7103, an material input portion 7105, an orifice 7106 and a spherically ground hemispherical radial outward flare 7107 on the outside of the nozzle near the orifice. The nozzle is made from free standing diamond.

Referring to FIGS. 72 a and 72 b, a cross sectional view and an end view, respectively, are provided of a nozzle or nozzle component 7201. The nozzle has a hemispherical end section, a cylindrical shank portion, an material input portion, an orifice and a flare-out on the outside of the nozzle near the orifice.

Referring to FIGS. 73 a and 73 b, a cross sectional view and an end view, respectively, are provided of a nozzle or nozzle component 7301. The nozzle has a hemispherical end section, a cylindrical shank portion, a material input portion, a substrate, a bore through the substrate and the diamond layer, an orifice and an arcuate flare-out on the outside of the nozzle near the orifice.

Referring to FIGS. 74 a and 74 b, a cross sectional view and an end view, respectively, are provided of a nozzle or nozzle component 7401. The nozzle has a hemispherical end section, a cylindrical shank portion, a material input portion, an orifice, a straight bore in the orifice, and a conical flare-out on the outside of the nozzle near the orifice.

Referring to FIGS. 75 a and 75 b, a cross sectional view and an end view, respectively, are provided of a nozzle or nozzle component 7501. The nozzle has a hemispherical end section, a cylindrical shank portion, a material input portion, a material reservoir 7502 internal to the nozzle, an orifice, and a straight bore in the orifice.

Referring to FIGS. 76 a and 76 b, a cross sectional view and an end view, respectively, are provided of a nozzle or nozzle component 7601. The nozzle has a hemispherical end section, a cylindrical shank portion, a material input portion, a reduced size material reservoir internal to the nozzle, an orifice, and a straight bore in the orifice.

Referring to FIGS. 77 aand 77 b, a cross sectional view and an end view, respectively, are provided of a nozzle or nozzle component 7701. The nozzle has a hemispherical end section, a cylindrical shank portion, a material input portion, a reduced size material reservoir internal to the nozzle, an orifice, and a blended flare-out in the orifice.

Referring to FIGS. 78 aand 78 b, a cross sectional view and an end view, respectively, are provided of a nozzle or nozzle component 7801. The nozzle has a hemispherical end section, a cylindrical shank portion, a material input portion, a reduced size material reservoir internal to the nozzle, an orifice, and a flare-in section prior to the orifice that leads to greater and greater constriction eventually terminating in the orifice.

Referring to FIGS. 79 a-79 d, a top view, right side view, end view and isometric view of a nozzle or nozzle component 7901 are depicted. The nozzle includes a body with a round orifice. The orifice opens into an end V-groove cut on the body that terminates at the orifice. Opposite there is a side V-groove apex cut.

Referring to FIGS. 80 a, 80 b and 80 c, a cross sectional side view, top view and side cross sectional view are depicted respectively of a nozzle 8001. The nozzle includes a base plate 8002 that forms the body of the nozzle and which may be metal or other appropriate material. A PDC rod 8003 is fixed within the base plate. Plugs 8004 keep the rod in place. A flow conduit 8005 passes through the PDC rod, providing diamond flow and contact surfaces in the nozzle. The conduit includes an orifice that is outwardly flared.

Referring to FIGS. 81 a and 81 b, a cross sectional view and an end view, respectively, are provided of a nozzle or nozzle component 8101. The nozzle has a tubular shape with an outer circumference and a longitudinal inner bore. The nozzle is made from free standing diamond.

Referring to FIGS. 82 a and 82 b, a cross sectional view and an end view, respectively, are provided of a nozzle or nozzle component 8201. The nozzle has a tubular shape with an outer circumference and a longitudinal inner bore. The nozzle includes a diamond rod with a bore in its interior, and an outer substrate. Plugs or caps may be used at the ends of the diamond rod.

Referring to FIGS. 83 a and 83 b, a cross sectional view and an end view, respectively, are provided of a nozzle or nozzle component 8301. The nozzle has a tubular shape with an outer circumference and a longitudinal inner bore. The nozzle includes a diamond rod with a bore in its interior, and an outer substrate.

Referring to FIGS. 84 a and 84 b, a cross sectional view and an end view, respectively, are provided of a nozzle or nozzle component 8401. The nozzle has a tubular shape with an outer circumference and a longitudinal inner bore. The nozzle includes a diamond rod with a bore in its interior, and an outer substrate. The diamond rod has been assembled from a series of individual diamond donuts or wheels or washers. Plugs or caps may be used at the ends of the diamond rod. Plugs or caps can be brazed, press fit, mechanically fixed, or bonded using an adhesive.

Referring to FIGS. 85 a and 85 b, a cross sectional view and an end view, respectively, are provided of a nozzle or nozzle component 8501. The nozzle 8501 has a longitudinal tubular body 8502 with an inner conduit or bore 8503 and a tapered distal dispensing end 8504. A diamond restraining shoulder 8506 at the proximal end can be used to fit the nozzle in a spray apparatus.

Referring to FIGS. 86 a and 86 b, a cross sectional view and an end view, respectively, are provided of a nozzle or nozzle component 8601. The nozzle has a longitudinal tubular body with an inner conduit or bore and a tapered distal dispensing end. A metal restraining shoulder at the proximal end can be used to fit the nozzle in a spray apparatus. The nozzle includes a substrate such as WC or CoCr or other suitable material 8602 and a diamond inner rod. A straight or radial conic tip may be used.

Referring to FIGS. 87 aand 87 b, a cross sectional view and an end view, respectively, are provided of a nozzle or nozzle component 8701. The nozzle has a longitudinal tubular body with an inner conduit or bore and a tapered distal dispensing end. A metal restraining shoulder at the proximal end can be used to fit the nozzle in a spray apparatus. The nozzle includes a substrate such as WC or CoCr or other suitable material 8602. The diamond inner rod is assembled from a series of diamond disks. A straight, radial conic or frustoconical tip may be used. A plug 8603 may be used at the proximal end near the shoulder.

FIG. 88 depicts a nozzle 8801 including its fluid flow 8802, body 8803, fitting 8804, tip retainer 8805 for retaining a diamond tip, PDC spray tip 8806 and orifice 8801.

FIG. 89 depicts a nozzle 8901 with components generally as previously mentioned including a distribution core 8902 that may have a plurality of conduits and a diamond spray tip 8903 with an orifice 8904. The distribution core and the tip may both be diamond if desired.

FIG. 90 depicts a nozzle 9001 including a diamond spray tip 9002 having an orifice 9003 with angled flared out opening and retainer 9004.

FIG. 91 depicts a nozzle 9101 including a diamond spray top 9003 having a bore and orifice 9103 and a retainer 9104. The angle of the flared out opening of the orifice determines spray pattern for the nozzle, and angles may be narrow such as 15 to 30 degrees, medium such as 50 to 100 degrees, wide such as 100 to 130 degrees, or otherwise.

FIG. 92 depicts a nozzle 9201 including a metal body 9203 and a diamond liner 9202 with an inner bore for fluid flow.

FIG. 93 a depicts a nozzle 9301, and FIG. 93 b depicts a cross sectional view of the nozzle 9301. The nozzle 9301 includes a metal body 9303 and a diamond liner 9302 with inner conduit passageway. The nozzle tip has a helical screw configuration.

FIGS. 94 a and 94 b depict a cross sectional side view and an end view, respectively, of a nozzle 9401 that includes a tubular PDC liner 9402. This nozzle provides a square spray pattern due to 4 V-grooves.

FIGS. 95 a and 95 b depict a cross sectional side view and an end view, respectively, of a nozzle 9501 that includes a tubular PDC liner 9502. This nozzle provides a wide angle spray pattern.

FIGS. 96 a and 96 b depict a cross sectional side view and an end view, respectively, of a nozzle 9601 that includes a tubular PDC liner 9602. This nozzle provides an oval spray pattern.

FIGS. 97 a and 97 b depict a cross sectional side view and an end view, respectively, of a nozzle 9701 that includes a tubular PDC liner 9402. The nozzle is for large capacity flow and a narrow spray angle such as 50-65 degrees. It includes a PDC liner and can be have a flow conduit from 1 inch to 9.5 inches in diameter.

FIGS. 98 a and 98 b depict a cross sectional side view and an end view, respectively, of a nozzle 9801 that includes a tubular PDC liner 9802. The nozzle has a mounting flange with bolt holes. This nozzle is for large capacity flow and a standard spray pattern (80 to 95 degrees).

FIGS. 99 a and 99 b depict a cross sectional side view and an end view, respectively, of a nozzle 9901 that includes a body 9904, a bore 9902, a dispersion valve 9903 within the bore of the body, an orifice 9907 and a diamond liner 9906 in the vicinity of the orifice. This nozzle provides wide angle spray.

FIGS. 100 a and 100 b depict a cross sectional side view and an end view, respectively, of a nozzle 10001 that includes a body, a bore, a dispersion valve within the bore of the body, an orifice and a diamond liner 10002 in the vicinity of the orifice. This nozzle provides a standard angle spray.

FIGS. 101 a and 101 b depict a cross sectional side view and an end view, respectively, of a nozzle 10101 that includes a body, a bore, a dispersion valve within the bore of the body, an orifice and a diamond liner 10102 in the vicinity of the orifice. This nozzle provides a narrow angle spray.

FIGS. 102 a and 102 b depict a cross sectional side view and an end view, respectively, of a nozzle 10201 that includes a 10201 body, a bore 10206, a high pressure tip retainer 10203, a tip 10204, a PDC liner 10205 and a tip gasket 10210. This nozzle provides high pressure spray.

FIGS. 103 a and 103 b depict a cross sectional side view and an end view, respectively, of a nozzle 10301 that includes a body, a bore, a tip retainer, a tip gasket, and a diamond liner 10302 at the orifice. This nozzle provides a flat spray.

FIGS. 104 a, 104 b and 104 c depict side, end and cross sectional side views, respectively, of a nozzle 10401 that includes a body 10402, a bore 10403, a diamond liner 10407 in the bore, and a diamond shield or deflector 10406. This nozzle may be used for dry spray powder application.

FIGS. 105 a and 105 b depict a cross sectional side view and an end view, respectively, of a nozzle 10501 that includes a body, a bore, a tip, a tip gasket, a tip retainer, and a diamond liner or conduit 10502 of the tip at the exit orifice. This nozzle provides high pressure spray.

FIGS. 106 a and 106 b depict a cross sectional side view and an end view, respectively, of a nozzle 10601 that includes a body 10602, a bore 10605, a cap 10603, an insert base such as WC 10604, a diamond dispersion insert 10608, a diamond orifice insert 10609 and an orifice 10609. This nozzle is useful for dry spray powder.

FIG. 107 a depicts a dispersion insert 10607 that may include a WC body 10607 a and a diamond dispersion end 10607 b.

FIG. 107 b depicts a diamond orifice insert 10608 with an inner bore or conduit.

FIGS. 108 a and 108 b depict a cross sectional side view and an end view, respectively, of a nozzle 10801 that includes a body, a bore, diamond liner or conduit 10802 in the bore, and a diamond deflector 10803 to provide angled spray diversion, such as from an angle of 0 to 60 degrees or otherwise.

FIG. 109 depicts a side view of an airless spray nozle that is handle mounted 10900. The nozzle includes an orifice 10901 and a diamond orifice insert 10902.

FIGS. 110 a and 110 b depict cross sectional side and end views, respectively, of an airless spray nozzle 11001. The nozzle includes a body and a bore, a diamond insert 11002 in the bore and an insert backer 11003. The insert backer 11003 has a diamond liner 11004 and a bore within it for material to travel through the backer, through the nozzle insert 11002 and out of the nozzle. A spray guide is provided distal to the nozzle insert.

FIGS. 111 a and 111 b depicts end and cross sectional side views respectively of an air atomizing pressure spray nozzle 11101 that peforms internal mixing of air and fluid, including a fluid cap 11102, an air flow channel 11103 through the fluid cap, a fluid bore 11104 through the fluid cap, a retaining ring 11110, a diamond fluid tip 11105, a nipple 11111 on the diamond fluid tip, an air cap 11106, an internal mixing chamber 11107, a diamond liner 11108 for the mixing chamber, and an exit orifice 11109. The air channel and exit orifice are adjacent inside the mixing chamber for internal mixing.

FIGS. 112 a and 112 b depicts end and cross sectional side views respectively of an air atomizing pressure spray nozzle 11201 that performs external mixing of air and fluid, including the aforementioned fluid cap, air cap and retaining ring. The nozzle also includes a diamond fluid tip 11202 with nipple and exit orifice. The air channel and exit orifice are adjacent outside the nozzle for external mixing.

FIGS. 113 a and 113 b depict cross sectional side and end views of a high pressure airless spray nozzle 11301, including a nozzle body 11302, bore 11303, retaining plug 11304, retaining ring 11305, diamond bore liner 11306, diamond nozzle insert 11307, and orifice.

FIGS. 114 a and 114 b depict cross sectional side and end views of a nozzle 11401, including a nozzle body 11402, liquid input 11403, air input 11404, electrode cap retainer 11405, electrode wire lead 11406, diamond liquid nozzle liner (tubular) 11407, electrode cap 11408, electrical insulator 11409, electrode driver 11410, insulating washer 11411, air exit orifice 11412, mixing chamber 11413, liquid exit orifice 11415, and diamond electrode cap orifice liner 11416. This nozzle may be used for electrostatic spray applications.

While the present devices and methods have been described and illustrated in conjunction with a number of specific configurations, those skilled in the art will appreciate that variations and modifications may be made without departing from the principles herein illustrated, described, and claimed. The present invention, as defined by the appended claims, may be embodied in other specific forms without departing from its spirit or essential characteristics. The configurations described herein are to be considered in all respects as only illustrative, and not restrictive. All changes which come within the meaning and range of equivalency of the claims are to be embraced within their scope. 

1-2. (canceled)
 3. A spray nozzle comprising: a nozzle body, a nozzle entry orifice through which a material to be sprayed can enter, a nozzle bore through which a material to be sprayed can pass, a nozzle exit orifice through which a material to be sprayed can exit, a sintered polycrystalline diamond compact bore liner in said bore for providing low wear, durable and long-lasting service in the nozzle, interstitial spaces in said diamond compact, solvent-catalyst metal in said interstitial spaces, chemical bonds in the sintered polycrystalline diamond compact bore liner, said chemical bonds including diamond-to-diamond bonds, diamond-to-metal bonds, and metal-to-metal bonds.
 4. The spray nozzle as recited in claim 3 wherein the nozzle entry orifice, nozzle bore and nozzle exit orifice each have an internal diameter.
 5. The spray nozzle as recited in claim 4 wherein the internal diameter of the entry orifice is greater than the internal diameter of the exit orifice.
 6. The spray nozzle of claim 5 wherein the internal diameter of the nozzle bore is reverse conical.
 7. The spray nozzle as recited in claim 4 wherein the internal diameter of the entry orifice is less than the internal diameter of the exit orifice.
 8. The spray nozzle as recited in claim 7 wherein the internal diameter of the nozzle bore is conical.
 9. The spray nozzle as recited in claim 3 wherein said diamond compact comprises diamond feedstock that has diamond particles that have a dimension in the range of less than about 1 nanometer to more than about 100 microns.
 10. The spray nozzle as recited in claim 3 further comprising CoCr solvent-catalyst metal in said interstitial spaces.
 11. The spray nozzle as recited in claim 3 further comprising tungsten carbide solvent-catalyst metal in said interstitial spaces.
 12. The spray nozzle as recited in claim 3 wherein at least some of said bonds are sp3 carbon bonds.
 13. The spray nozzle as recited in claim 1 wherein said diamond compact includes diamond sintered to a substrate.
 14. The spray nozzle as recited in claim 3 wherein said diamond compact is constructed from free standing diamond that is not sintered to a substrate.
 15. A spray nozzle comprising: a nozzle body, a nozzle entry orifice through which a material to be sprayed can enter, a nozzle bore through which a material to be sprayed can pass, a nozzle exit orifice through which a material to be sprayed can exit, a sintered polycrystalline diamond compact nozzle tip at said exit orifice, interstitial spaces in said diamond compact, solvent-catalyst metal located in said interstitial spaces, chemical bonds in the sintered polycyrstalline diamond compact nozzle tip, said chemical bonds including diamond-to-diamond bonds, diamond-to-metal bonds, and metal-to-metal bonds, and wherein material to be sprayed travels from said bore, through said sintered polycrystalline diamond compact nozzle tip and out said exit orifice.
 16. The spray nozzle as recited in claim 15 wherein said diamond compact comprises diamond feedstock that has diamond particles that have a dimension in the range of less than about 1 nanometer to more than about 100 microns.
 17. The spray nozzle as recited in claim 15 further comprising CoCr solvent-catalyst metal in said interstitial spaces.
 18. The spray nozzle as recited in claim 15 further comprising tungsten carbide solvent-catalyst metal in said interstitial spaces.
 19. The spray nozzle as recited in claim 15 wherein at least some of said bonds are sp3 carbon bonds.
 20. The spray nozzle as recited in claim 15 wherein said diamond compact includes diamond sintered to a substrate.
 21. The spray nozzle as recited in claim 15 wherein said diamond compact is constructed from free standing diamond that is not sintered to a substrate.
 22. The spray nozzle as recited in claim 15 wherein the nozzle tip at said exit orifice is a hemispherical cup.
 23. The spray nozzle as recited in claim 22 wherein the nozzle tip at said exit orifice further comprises an elongated member extending from said hemispherical cup.
 24. The spray nozzle as recited in claim 22 wherein the nozzle tip further comprises a concave relief surrounding said exit orifice.
 25. A spray nozzle comprising: a sintered polycrystalline diamond compact nozzle body, a bore through said nozzle body, at least a portion of said bore presenting diamond as the material that contacts fluid flowing through said bore. 